Failure analysis of cracking in wheel rims - material and manufacturing aspects

被引：25

作者：

Bhattacharyya, Sandip ^{[1
]}

Adhikary, M. ^{[1
]}

Das, M. B. ^{[1
]}

Sarkar, Sudipto ^{[1
]}

机构：

[1] Tata Steel Ltd, R&D & Sci Serv, Jamshedpur 831007, Bihar, India

来源：

ENGINEERING FAILURE ANALYSIS | 2008年 / 15卷 / 05期

关键词：

thinning; necking; cracking; weld; heat affected zone;

D O I：

10.1016/j.engfailanal.2007.04.007

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Manufacturing of wheel in automotive industries demands no-flaw wheels. However, process as well as material deficiency in varying ratios of influence has been the counteracting factors in producing flawless wheel components. Tube and tubeless wheels for light and medium commercial vehicles are manufactured by cold forming of slit hot rolled strips from low carbon steel with or without micro alloying. During manufacturing and forming of the strips, cracking of wheel rims is a major problem at the production line. The paper discusses about one of the failure types in wheel rims, where the wheel rim thins down locally and cracks at the weld. (C) 2007 Elsevier Ltd. All rights reserved.

引用

页码：547 / 554

页数：8

共 50 条

[31] Failure analysis of handhole flange cracking
Zhang, Yuan
Shang, Xiandong
Song, Mingda
Sun, Zhiwei
Xu, Shugen
ENGINEERING FAILURE ANALYSIS, 2019, 96 : 100 - 108
[32] Design and material aspects of oilwell drillstring failure
Macdonald, K.A.
Deans, W.F.
Journal of Offshore Technology, 1995, 3 (01): : 2 - 4
[33] Nonlinear analysis of the GFRP material wheel hub
Dong Yun-Feng
Wang Xun-Chang
Yang Kun
Qu Xing-Tian
2015 7TH INTERNATIONAL CONFERENCE ON MECHANICAL AND ELECTRONICS ENGINEERING (ICMEE 2015), 2015, 31
[34] Analysis of failure in manufacturing machinery
Sulaiman, S.
Ismail, N. Abidin
2ND INTERNATIONAL CONFERENCE ON MECHANICAL ENGINEERING RESEARCH (ICMER 2013), 2013, 50
[35] MICROROTATION ANALYSIS APPLIED TO MATERIAL CRACKING AND TOUGHNESS
WANG, C
CHEN, ZD
INTERNATIONAL JOURNAL OF FRACTURE, 1992, 54 (04) : 359 - 369
[36] Failure analysis of fifth wheel coupling system
Reboh, Y.
Griza, S.
Reguly, A.
Strohaecker, T. R.
ENGINEERING FAILURE ANALYSIS, 2008, 15 (04) : 332 - 338
[37] Failure analysis of a cast steel railway wheel
Fuoco, R
Ferreira, MM
Azevedo, CRF
ENGINEERING FAILURE ANALYSIS, 2004, 11 (06) : 817 - 828
[38] FAILURE ANALYSIS OF BUCKETS OF A WHEEL-EXCAVATOR.
Chaulia, P.B.
Sen, K.K.
Dasgupta, S.P.
1600, (57):
[39] An Ordinary State-Based Peridynamic Model for Fatigue Cracking of Ferrite and Pearlite Wheel Material
Han, Junzhao
Chen, Wenhua
APPLIED SCIENCES-BASEL, 2020, 10 (12):
[40] Cleaning aspects of material choice for high end mask manufacturing
Nesladek, Pavel
Osborne, Steve
Ruemmelin, Stefan
28TH EUROPEAN MASK AND LITHOGRAPHY CONFERENCE, 2012, 8352

← 1 2 3 4 5 →