Failure analysis of cracking in wheel rims - material and manufacturing aspects

被引：25

作者：

Bhattacharyya, Sandip ^{[1
]}

Adhikary, M. ^{[1
]}

Das, M. B. ^{[1
]}

Sarkar, Sudipto ^{[1
]}

机构：

[1] Tata Steel Ltd, R&D & Sci Serv, Jamshedpur 831007, Bihar, India

来源：

ENGINEERING FAILURE ANALYSIS | 2008年 / 15卷 / 05期

关键词：

thinning; necking; cracking; weld; heat affected zone;

D O I：

10.1016/j.engfailanal.2007.04.007

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Manufacturing of wheel in automotive industries demands no-flaw wheels. However, process as well as material deficiency in varying ratios of influence has been the counteracting factors in producing flawless wheel components. Tube and tubeless wheels for light and medium commercial vehicles are manufactured by cold forming of slit hot rolled strips from low carbon steel with or without micro alloying. During manufacturing and forming of the strips, cracking of wheel rims is a major problem at the production line. The paper discusses about one of the failure types in wheel rims, where the wheel rim thins down locally and cracks at the weld. (C) 2007 Elsevier Ltd. All rights reserved.

引用

页码：547 / 554

页数：8

共 50 条

[41] Failure analysis and redesign of the bucket wheel excavator two-wheel bogie
Bosnjak, Srdan
Petkovic, Zoran
Zrnic, Nenad
Pantelic, Milorad
Obradovic, Aleksandar
ENGINEERING FAILURE ANALYSIS, 2010, 17 (02) : 473 - 485
[42] Probabilistic Aspects of Modeling and Analysis of Grinding Wheel Wear
Kacalak, Wojciech
Lipinski, Dariusz
Szafraniec, Filip
Banaszek, Kamil
Rypina, Lukasz
MATERIALS, 2022, 15 (17)
[43] Cracking Failure Analysis of Ethylene Oxide Evaporator
Du Chen-yang
Wang Hui
PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, PVP 2012, VOL 1, 2012, : 519 - 524
[44] CRACKING AND FAILURE ANALYSIS OF MASONRY ARCH BRIDGES
LOO, YC
YANG, Y
JOURNAL OF STRUCTURAL ENGINEERING-ASCE, 1991, 117 (06): : 1641 - 1659
[45] Stochastic aspects of localised failure:: material and boundary imperfections
Gutiérrez, MA
De Borst, R
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2000, 37 (48-50) : 7145 - 7159
[46] Mechanics and material aspects in predicting serviceability limited by stress-corrosion cracking
Leis, BN
Parkins, RN
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1998, 21 (05) : 583 - 601
[47] The business aspects of failure analysis
Frank, R
Lee, T
ISTFA '97 - PROCEEDINGS OF THE 23RD INTERNATIONAL SYMPOSIUM FOR TESTING AND FAILURE ANALYSIS, 1997, : 255 - 266
[48] Failure analysis of corrosion cracking and simulated testing for a fluid catalytic cracking unit
Hua Chen1)
Journal of University of Science and Technology Beijing(English Edition), 2005, (02) : 172 - 177
[49] Failure analysis of corrosion cracking and simulated testing for a fluid catalytic cracking unit
Chen, H
Li, XG
Dong, CF
Li, M
Yang, JW
JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 2005, 12 (02): : 172 - 177
[50] Failure analysis of an abrasive cut-off wheel
Riga, AT
Scott, CG
ENGINEERING FAILURE ANALYSIS, 2001, 8 (03) : 237 - 243

← 1 2 3 4 5 →