Failure analysis of cracking in wheel rims - material and manufacturing aspects

被引：25

作者：

Bhattacharyya, Sandip ^{[1
]}

Adhikary, M. ^{[1
]}

Das, M. B. ^{[1
]}

Sarkar, Sudipto ^{[1
]}

机构：

[1] Tata Steel Ltd, R&D & Sci Serv, Jamshedpur 831007, Bihar, India

来源：

ENGINEERING FAILURE ANALYSIS | 2008年 / 15卷 / 05期

关键词：

thinning; necking; cracking; weld; heat affected zone;

D O I：

10.1016/j.engfailanal.2007.04.007

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Manufacturing of wheel in automotive industries demands no-flaw wheels. However, process as well as material deficiency in varying ratios of influence has been the counteracting factors in producing flawless wheel components. Tube and tubeless wheels for light and medium commercial vehicles are manufactured by cold forming of slit hot rolled strips from low carbon steel with or without micro alloying. During manufacturing and forming of the strips, cracking of wheel rims is a major problem at the production line. The paper discusses about one of the failure types in wheel rims, where the wheel rim thins down locally and cracks at the weld. (C) 2007 Elsevier Ltd. All rights reserved.

引用

页码：547 / 554

页数：8

共 50 条

[11] Metallurgical Evaluation and Failure Analysis of Cracking in Wheel Rim SPFH590 Steel
Janarthanan, Vajiravelu
Selvakumar, Gurusamy
Vijayan, Sundaravel
Sumathi, Muniasamy
MATERIALS TESTING, 2020, 62 (02) : 117 - 122
[12] Structural and fatigue analysis of car wheel rims with carbon fibre composites
Poodipeddi, S. V. K. S. V. Krishna Kiran
Singampalli, Amarthya
Rayala, Lalith Sai Madhav
Ravula, Surya Sudarsan Naveen
WORLD JOURNAL OF ENGINEERING, 2024, 21 (03) : 503 - 509
[13] Probabilistic aspects of material failure
Bizup, DF
Singpurwalla, ND
PROBABILISTIC MECHANICS & STRUCTURAL RELIABILITY: PROCEEDINGS OF THE SEVENTH SPECIALTY CONFERENCE, 1996, : 474 - 477
[14] An Analysis of the Failure of a Wheel Hub
Herz, M.
Triesch, G.
PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY, 2012, 49 (06): : 377 - 383
[15] Failure analysis of blower wheel
Zhang, Z.
Su, M.
Zhong, Q.P.
2001, Beijing Institute of Aeronautical Materials (BIAM)
[16] Metallographic Fractographic Aspects of Railway Wheel Failure.
Slesar, Milan
Sevcik, Antonin
Stefan, Blazej
Sroka, Frantisek
Hutnicke listy, 1986, 41 (01): : 41 - 46
[17] Verification of material composition and manufacturing process of carbon fibre wheel
Maňas L.
Rusnáková S.
Javořík J.
Žaludek M.
Fojtl L.
Manufacturing Technology, 2019, 19 (02): : 280 - 283
[18] Failure analysis of the cracking parts
Sun, Wei-Lian, 1600, Northeast University (35):
[19] MATERIAL ASPECTS OF FRICTION AND WEAR IN MANUFACTURING PROCESSES
SCHEY, JA
JOURNAL OF METALS, 1980, 32 (01): : 28 - 33
[20] Meshfree cohesive cracking method for dynamic material failure
Wang, S.
INTERNATIONAL JOURNAL OF MECHANICS AND MATERIALS IN DESIGN, 2010, 6 (02) : 103 - 111

← 1 2 3 4 5 →