Failure analysis of a cast steel railway wheel

被引：23
|
作者：
Fuoco, R [1 ]
Ferreira, MM [1 ]
Azevedo, CRF [1 ]
机构：
[1] Inst Pesquisas Tecnol Estado Sao Paulo SA, Div Met, BR-01064970 Sao Paulo, Brazil
来源：
ENGINEERING FAILURE ANALYSIS | 2004年 / 11卷 / 06期
基金：
巴西圣保罗研究基金会;
关键词：
failure analysis; fractography; cast steel; fatigue; railway engineering;
D O I：
10.1016/j.engfailanal.2004.03.004
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The failure analysis of a broken railway pearlitic cast steel railway wheel, which was involved in a train derailment, has been investigated. The fractographic results near the fracture origin of the wheel have been compared to the regions of stable (fatigue) and unstable crack propagation of cast steel fracture toughness samples. The macro and microfractographic features of the broken wheel did not show any evidence of the occurrence of a fatigue mechanism, indicating that its fracture was caused by transgranular cleavage fracture, as a consequence of the train derailment. (C) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码：817 / 828
页数：12
相关论文
共 50 条
  • [1] Failure analysis of railway wheel tread
    Kwon, Seok-Jin
    Lee, Dong-Hyung
    Kwon, Sung-Tae
    Goo, Byoeng-Chun
    ADVANCED NONDESTRUCTUVE EVALUATION I, PTS 1 AND 2, PROCEEDINGS, 2006, 321-323 : 649 - 653
  • [2] Failure modes analysis of railway wheel
    Spiroiu, Marius-Adrian
    Nicolescu, Mircea
    22ND INTERNATIONAL CONFERENCE ON INNOVATIVE MANUFACTURING ENGINEERING AND ENERGY - IMANE&E 2018, 2018, 178
  • [3] DISTRIBUTION OF HYDROGEN IN CAST AND HOT-WORKED RAILWAY WHEEL STEEL
    SHAPOVALOV, VI
    TROFIMENKO, VV
    ANTIPOVA, NV
    STEEL IN THE USSR, 1981, 11 (04): : 244 - 245
  • [4] A failure analysis study of cast steel railway couplings used for coal transportation
    Infante, V
    Branco, CM
    Brito, AS
    Morgado, TL
    ENGINEERING FAILURE ANALYSIS, 2003, 10 (04) : 475 - 489
  • [5] Fatigue crack failure analysis of wrought steel railway wheel with web plate hole
    Zheng, HX
    Xie, JL
    Wang, WJ
    Proceedings of the International Conference on Mechanical Engineering and Mechanics 2005, Vols 1 and 2, 2005, : 1471 - 1474
  • [6] Cyclic Deformation Behaviour of China Railway Grade B Cast Steel Wheel
    Zhao, Y. X.
    Song, G. X.
    MATERIALS ENGINEERING FOR ADVANCED TECHNOLOGIES, PTS 1 AND 2, 2011, 480-481 : 306 - +
  • [7] Random Mechanical Properties of China Railway Grade B Cast Steel Wheel
    Liu, J. Y.
    Zhao, Y. X.
    Song, G. X.
    MATERIALS ENGINEERING FOR ADVANCED TECHNOLOGIES, PTS 1 AND 2, 2011, 480-481 : 179 - +
  • [8] Random Fatigue Limits of China Railway Grade B Cast Steel Wheel
    Zhao, Y. X.
    Yang, B.
    Wang, Z. G.
    MATERIALS ENGINEERING FOR ADVANCED TECHNOLOGIES, PTS 1 AND 2, 2011, 480-481 : 347 - +
  • [9] Fatigue Reliability Curves for China Railway Grade B Cast Steel Wheel
    Liang, H. Q.
    Zhao, Y. X.
    Li, Y.
    MATERIALS ENGINEERING FOR ADVANCED TECHNOLOGIES, PTS 1 AND 2, 2011, 480-481 : 352 - +
  • [10] Chemical Composition and Physical Properties for China Railway Grade B Cast Steel Wheel
    Zhao, Y. X.
    Yang, B.
    Song, G. X.
    MATERIALS ENGINEERING FOR ADVANCED TECHNOLOGIES, PTS 1 AND 2, 2011, 480-481 : 42 - +
12345