Failure analysis of a cast steel railway wheel

被引：23
|
作者：
Fuoco, R [1 ]
Ferreira, MM [1 ]
Azevedo, CRF [1 ]
机构：
[1] Inst Pesquisas Tecnol Estado Sao Paulo SA, Div Met, BR-01064970 Sao Paulo, Brazil
来源：
ENGINEERING FAILURE ANALYSIS | 2004年 / 11卷 / 06期
基金：
巴西圣保罗研究基金会;
关键词：
failure analysis; fractography; cast steel; fatigue; railway engineering;
D O I：
10.1016/j.engfailanal.2004.03.004
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The failure analysis of a broken railway pearlitic cast steel railway wheel, which was involved in a train derailment, has been investigated. The fractographic results near the fracture origin of the wheel have been compared to the regions of stable (fatigue) and unstable crack propagation of cast steel fracture toughness samples. The macro and microfractographic features of the broken wheel did not show any evidence of the occurrence of a fatigue mechanism, indicating that its fracture was caused by transgranular cleavage fracture, as a consequence of the train derailment. (C) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码：817 / 828
页数：12
相关论文
共 50 条
  • [31] Production of High-Quality Wheel Steel. Part 1. Production Aspects of Continuously-Cast Billet Quality for Railway Wheel Manufacture
    Pumpyanskiy, D. A.
    Tyutyunik, S. V.
    Kolokolov, E. A.
    Mescheryachenko, A. A.
    Murzin, I. S.
    Emel'yanov, V. V.
    Belonozhko, S. S.
    Arsenkin, A. M.
    METALLURGIST, 2021, 65 (1-2) : 13 - 20
  • [32] NONMETALLIC INCLUSIONS AND FAILURE OF CAST STEEL
    VOLCHOK, IP
    SHULTE, YA
    PINCHUK, EI
    RUSSIAN METALLURGY-METALLY-USSR, 1970, (01): : 71 - &
  • [33] Characterization of a New Steel for Class D Forged Railway Wheel
    Rezende, A. B.
    Miranda, R. S.
    Fonseca, S. T.
    Mei, P. R.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2025, 34 (01) : 46 - 61
  • [34] Optimization of strength and toughness of railway wheel steel by alloy design
    Zeng, Dongfang
    Lu, Liantao
    Gong, Yanhua
    Zhang, Ning
    Gong, Yubin
    MATERIALS & DESIGN, 2016, 92 : 998 - 1006
  • [35] Fatigue Investigation on Railway Wheel Steel with White Etching Layer
    Y. M. Zhang
    Z. M. Xiao
    M. Fan
    International Journal of Steel Structures, 2020, 20 : 80 - 88
  • [36] Mixed mode fatigue crack propagation in a railway wheel steel
    Peixoto, Daniel F. C.
    de Castro, Paulo M. S. T.
    XV PORTUGUESE CONFERENCE ON FRACTURE, PCF 2016, 2016, 1 : 150 - 157
  • [37] Effect of material strength on shelling property of railway wheel steel
    Kato, Takanori
    Makino, Taizo
    Zairyo/Journal of the Society of Materials Science, Japan, 2012, 61 (08) : 698 - 703
  • [38] Analysis of ultimate load and mechanisms of failure in large cast steel joints
    Lu, Yun-Xiang
    Cai, Yuan-Qi
    Li, Ming-Fang
    Liao, Feng-Lian
    Chongqing Daxue Xuebao/Journal of Chongqing University, 2010, 33 (12): : 71 - 77
  • [39] SIMULATION OF RAILWAY WHEEL HEATING ON BRAKING BY CAST IRON AND COMPOSITE BRAKE BLOCKS
    Suchanek, Andrej
    Harusinec, Jozef
    Loulova, Maria
    XXIII KONFERENCE S MEZINARODNI UCASTI: SOUCASNE PROBLEMY V KOLEJOVYCH VOZIDLECH/ 23RD CONFERENCE: CURRENT PROBLEMS IN RAIL VEHICLES 2017, 2017, : 371 - 378
  • [40] Effect of elevated temperature on shelling property of railway wheel steel
    Kato, T.
    Kato, H.
    Makino, T.
    WEAR, 2016, 366 : 359 - 367
12345