The Influence of the Interface on Fracture Parameters

被引：1
|
作者：
Marsavina, L. [1 ]
Sadowski, T. [1 ]
机构：
[1] Lublin Univ Technol, Fac Civil & Sanit Engn, PL-20618 Lublin, Poland
来源：
DAMAGE AND FRACTURE MECHANICS: FAILURE ANALYSIS OF ENGINEERING MATERIALS AND STRUCTURES | 2009年
关键词：
Crack; Bi-Material Interface; Singularity Order; Stress Intensity Factor; LOADED CRACK; BIMATERIAL; PENETRATION;
D O I：
10.1007/978-90-481-2669-9_26
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The presence of cracks has a major impact on the reliability of advanced materials, like fiber or particle reinforced ceramic composites, and laminated ceramics. The understanding of the failure mechanisms is very important, as much as the estimation of fracture parameters at the tip of the crack approaching an interface. This paper presents the numerical results for singularity order, asymptotic stress field and fracture parameters for a crack ending on a bi-material ceramic interface. The effect of bi-axial loading on asymptotic stress field and stress intensity factors was investigated.
引用
收藏
页码：245 / 254
页数：10
相关论文
共 50 条
  • [41] Influence of fracture parameters on hydraulic shear seepage characteristics of granite
    Tang, Jupeng
    Yu, Honghao
    Wei, Zhihao
    Zhang, Xiao
    CASE STUDIES IN THERMAL ENGINEERING, 2024, 56
  • [42] The influence of some technological parameters on the fracture toughness of ceramic materials
    Goanta, Viorel
    Mares, Marian
    STRUCTURAL ANALYSIS OF ADVANCED MATERIALS, 2010, 446 : 11 - 21
  • [43] Influence of shear parameters on mixed-mode fracture of concrete
    Gálvez, JC
    Cendón, DA
    Planas, J
    INTERNATIONAL JOURNAL OF FRACTURE, 2002, 118 (02) : 163 - 189
  • [44] Influence of metallurgical parameters on the fracture toughness of stainless steel welds
    Ould, P
    Balladon, P
    ECF 12: FRACTURE FROM DEFECTS, VOLS. I-III, 1998, : 901 - 906
  • [45] Influence of FSSW parameters on fracture mechanisms of 5182 aluminium welds
    Bozzi, S.
    Helbert-Etter, A. L.
    Baudin, T.
    Klosek, V.
    Kerbiguet, J. G.
    Criqui, B.
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2010, 210 (11) : 1429 - 1435
  • [46] Interface fracture of sandwich composites: Influence of MWCNT sonicated epoxy resin
    Patra, Alak
    Mitra, Nilanjan
    COMPOSITES SCIENCE AND TECHNOLOGY, 2014, 101 : 94 - 101
  • [47] Size effect and influence of aggregate roughness in interface fracture of concrete composites
    Trende, U
    Buyukozturk, O
    ACI MATERIALS JOURNAL, 1998, 95 (04) : 331 - 338
  • [48] Influence of the interface and fiber spacing on the fracture behavior of glass matrix composites
    Univ of Dayton, Dayton, United States
    Mater Eval, 9 (1045-1051):
  • [49] THE INFLUENCE OF HYDROGEN AND THE INTERFACE PHASE ON FRACTURE IN TI CODE-12
    MOODY, NR
    GREULICH, FA
    ROBINSON, SL
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1984, 15 (10): : 1955 - 1958
  • [50] Influence of manufacturing parameters of knitted compression fabric on interface pressure
    Barhoumi, H.
    Marzougui, S.
    Ben Abdessalem, S.
    INDIAN JOURNAL OF FIBRE & TEXTILE RESEARCH, 2018, 43 (04) : 426 - 433
12345