The Influence of the Interface on Fracture Parameters

被引：1
|
作者：
Marsavina, L. [1 ]
Sadowski, T. [1 ]
机构：
[1] Lublin Univ Technol, Fac Civil & Sanit Engn, PL-20618 Lublin, Poland
来源：
DAMAGE AND FRACTURE MECHANICS: FAILURE ANALYSIS OF ENGINEERING MATERIALS AND STRUCTURES | 2009年
关键词：
Crack; Bi-Material Interface; Singularity Order; Stress Intensity Factor; LOADED CRACK; BIMATERIAL; PENETRATION;
D O I：
10.1007/978-90-481-2669-9_26
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The presence of cracks has a major impact on the reliability of advanced materials, like fiber or particle reinforced ceramic composites, and laminated ceramics. The understanding of the failure mechanisms is very important, as much as the estimation of fracture parameters at the tip of the crack approaching an interface. This paper presents the numerical results for singularity order, asymptotic stress field and fracture parameters for a crack ending on a bi-material ceramic interface. The effect of bi-axial loading on asymptotic stress field and stress intensity factors was investigated.
引用
收藏
页码：245 / 254
页数：10
相关论文
共 50 条
  • [31] Determination of fracture parameters for interface cracks in transverse isotropic magnetoelectroelastic composites
    Lei, Jun
    Sun, Pengbo
    Bui, Tinh Quoc
    CURVED AND LAYERED STRUCTURES, 2015, 2 (01) : 271 - 278
  • [32] Influence of type of aggregate and surface roughness on the interface fracture properties
    Rao, G. Appa
    Prasad, B.K. Raghu
    Materials and Structures/Materiaux et Constructions, 2004, 37 (05): : 328 - 334
  • [33] Influence of type of aggregate and surface roughness on the interface fracture properties
    G. Appa Rao
    B. K. Raghu Prasad
    Materials and Structures, 2004, 37 : 328 - 334
  • [34] Influence of type of aggregate and surface roughness on the interface fracture properties
    Rao, GA
    Prasad, BKR
    MATERIALS AND STRUCTURES, 2004, 37 (269) : 328 - 334
  • [35] Interface energy and its influence on interface fracture between metal and ceramic thin films in nanoscale
    Liang, L. H.
    You, X. M.
    Ma, H. S.
    Wei, Y. G.
    JOURNAL OF APPLIED PHYSICS, 2010, 108 (08)
  • [36] Influence of interface roughness geometrical parameters on the shear behaviour of old and new concrete interface
    Ayinde O.O.
    Wu E.
    Zhou G.
    Malidadi T.
    Asian Journal of Civil Engineering, 2022, 23 (2) : 229 - 247
  • [37] Interface fracture
    Lane, M
    ANNUAL REVIEW OF MATERIALS RESEARCH, 2003, 33 : 29 - 54
  • [38] Analytical fracture parameters of two unequal collinear interface cracks in an orthotropic bimaterial
    Tafreshi, Azam
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2022, 121
  • [39] The influence of the fracture morphological parameters on bending break energy of polystyrene
    Xu, T
    Yu, J
    Luo, Z
    Wang, L
    Jin, ZH
    ACTA POLYMERICA SINICA, 1999, (02) : 141 - 145
  • [40] Influence of fracture parameters on inflow performance of fractured horizontal wells
    Wang, Zhi-Ming
    Qi, Zhen-Lin
    Wei, Jian-Guang
    Jin, Hui
    Zhongguo Shiyou Daxue Xuebao (Ziran Kexue Ban)/Journal of China University of Petroleum (Edition of Natural Science), 2010, 34 (01): : 73 - 78
12345