Environmentally assisted degradation spinodal copper alloy C72900

被引：20

作者：

Johnsen, Roy ^{[1
]}

Lange, Torstein ^{[2
]}

Stenerud, Gaute ^{[1
]}

Olsen, Jim Stian ^{[1
,3
]}

机构：

[1] Norwegian Univ Sci & Technol, Trondheim, Norway

[2] SINTEF, Trondheim, Norway

[3] Aker Solut, Fornebu, Norway

来源：

CORROSION SCIENCE | 2018年 / 142卷

关键词：

Copper; Hydrogen embrittlement; Stress corrosion; Sulfide cracking; Cathodic protection; De-alloying; CU-15NI-8SN ALLOY; DISCONTINUOUS PRECIPITATION; DECOMPOSITION;

D O I：

10.1016/j.corsci.2018.06.031

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this work, a spinodal Copper alloy - C72900, was tested to investigate the resistance against environmentally assisted degradation. The material was tested according to ISO 15156-3 Level V in sour H2S solution and to cathodic polarization in simulated seawater with stressed samples. The results showed no indications of hydrogen stress cracking under cathodic polarization in seawater. However, cracks up to 3 mm deep were found on the samples exposed to sour H2S environment. Energy Dispersive Spectroscopy showed severe depletion of copper close to the cracks which is associated with selective corrosion. Stress corrosion cracking was the dominating crack mechanism in the ISO 15156-3 Level V test.

引用

页码：45 / 55

页数：11

共 50 条

[31] Spinodal liquid phase separation enabling dissimilar resistance spot welding of immiscible iron and copper alloy system
Taghavi, Sahand
Pouranvari, Majid
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2023, 28 (02) : 98 - 107
[32] Carbon diffusivity and kinetics of spinodal decomposition of martensite in a model Fe-Ni-C alloy
Maugis, P.
Danoix, F.
Dumont, M.
Curelea, S.
Cazottes, S.
Zapolsky, H.
Goune, M.
MATERIALS LETTERS, 2018, 214 : 213 - 216
[33] Numerical simulation of the spinodal decomposition in hypothetical A-B and A-B-C alloy systems
Avila-Davila, E. O.
Lezama-Alvarez, S.
Saucedo-Munoz, M. L.
Lopez-Hirata, V. M.
Gonzalez-Velazquez, J. L.
Perez-Labra, M.
REVISTA DE METALURGIA, 2012, 48 (03) : 223 - 236
[34] An experimental-numerical screening method for assessing environmentally assisted degradation in high strength steels
Halilovic, Armin E.
Faleskog, Jonas
Boasen, Magnus
Efsing, Pal
ENGINEERING FRACTURE MECHANICS, 2021, 245
[35] An experimental-numerical screening method for assessing environmentally assisted degradation in high strength steels
Halilović, Armin E.
Faleskog, Jonas
Boåsen, Magnus
Efsing, Pål
Halilović, Armin E. (arminh@kth.se), 1600, Elsevier Ltd (245):
[36] Environmentally assisted dynamic embrittlement in a long range ordered Ni-Mo-Cr alloy
Dymek, S
Wróbel, M
Dollar, M
SCRIPTA MATERIALIA, 2000, 43 (04) : 343 - 348
[37] Environmentally assisted cracking of 3.5NiCrMoV low alloy steel under cyclic straining
Kondo, Y
Bodai, M
Takei, M
Sugita, Y
Inagaki, H
EFFECTS OF THE ENVIRONMENT ON THE INITIATION OF CRACK GROWTH, 1997, 1298 : 120 - 134
[38] Environmentally Assisted Cracking of Alloy 7050-T7451 Exposed to Aqueous Chloride Solutions
Reinhold Braun
Metallurgical and Materials Transactions A, 2016, 47 : 1367 - 1377
[39] Effects of Chromate and Non-Chromate Coating Systems on Environmentally Assisted Fatigue of an Aluminum Alloy
Joel J. Schubbe
Sophoria N. Westmoreland
Journal of Materials Engineering and Performance, 2014, 23 : 3534 - 3540
[40] Micro-mechanical State at Tip of Environmentally Assisted Cracking in Nickel-based Alloy
He, Xue
Li Yongqiang
RARE METAL MATERIALS AND ENGINEERING, 2016, 45 (03) : 537 - 541

← 1 2 3 4 5 →