Environmentally assisted degradation spinodal copper alloy C72900

被引：20

作者：

Johnsen, Roy ^{[1
]}

Lange, Torstein ^{[2
]}

Stenerud, Gaute ^{[1
]}

Olsen, Jim Stian ^{[1
,3
]}

机构：

[1] Norwegian Univ Sci & Technol, Trondheim, Norway

[2] SINTEF, Trondheim, Norway

[3] Aker Solut, Fornebu, Norway

来源：

CORROSION SCIENCE | 2018年 / 142卷

关键词：

Copper; Hydrogen embrittlement; Stress corrosion; Sulfide cracking; Cathodic protection; De-alloying; CU-15NI-8SN ALLOY; DISCONTINUOUS PRECIPITATION; DECOMPOSITION;

D O I：

10.1016/j.corsci.2018.06.031

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this work, a spinodal Copper alloy - C72900, was tested to investigate the resistance against environmentally assisted degradation. The material was tested according to ISO 15156-3 Level V in sour H2S solution and to cathodic polarization in simulated seawater with stressed samples. The results showed no indications of hydrogen stress cracking under cathodic polarization in seawater. However, cracks up to 3 mm deep were found on the samples exposed to sour H2S environment. Energy Dispersive Spectroscopy showed severe depletion of copper close to the cracks which is associated with selective corrosion. Stress corrosion cracking was the dominating crack mechanism in the ISO 15156-3 Level V test.

引用

页码：45 / 55

页数：11

共 50 条

[21] STRESS RELAXATION IN BENDING OF COPPER-NICKEL-TIN ALLOY STRIP STRENGTHENED BY SPINODAL DECOMPOSITION.
Fox, Alfred
1600, (07):
[22] STRESS-RELAXATION IN BENDING OF COPPER-NICKEL-TIN ALLOY STRIP STRENGTHENED BY SPINODAL DECOMPOSITION
FOX, A
JOURNAL OF TESTING AND EVALUATION, 1979, 7 (05) : 286 - 290
[23] Environmentally assisted "in-bulk" steel degradation of long term service gas trunkline
Nykyforchyn, H.
Lunarska, E.
Tsyrulnyk, O. T.
Nikiforov, K.
Genarro, M. E.
Gabetta, G.
ENGINEERING FAILURE ANALYSIS, 2010, 17 (03) : 624 - 632
[24] Degradation of copper/silver alloy thin films induced by annealing
Snyder, S. T.
King, A. H.
DEGRADATION PROCESSES IN NANOSTRUCTURED MATERIALS, 2006, 887 : 261 - +
[25] Understanding the role of matrix precipitates on the environmentally assisted cracking behavior of AA 7050 alloy
Shukla, Shweta
Jaya, Balila Nagamani
Raja, V. S.
CORROSION SCIENCE, 2022, 201
[26] Effect of water chemistry on environmentally assisted cracking in Alloy 600 in simulated PWR environments
Lidar, P
König, M
Engström, J
Gott, K
PROCEEDINGS OF THE NINTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 1999, : 125 - 130
[27] Copper(II)-Assisted Degradation of Pheophytin a by Reactive Oxygen Species
Orzel, Lukasz
Drzewiecka-Matuszek, Agnieszka
Rutkowska-Zbik, Dorota
Krasowska, Aneta
Fiedor, Leszek
van Eldik, Rudi
Stochel, Grazyna
INTERNATIONAL JOURNAL OF MOLECULAR SCIENCES, 2024, 25 (03)
[28] The effect of corrosion inhibiting pigments on environmentally assisted cracking of high strength aluminum alloy
Liu, XF
Huang, SJ
Gu, HC
CORROSION SCIENCE, 2003, 45 (09) : 1921 - 1938
[29] Development of high strength AA 7010 aluminum alloy resistant to environmentally assisted cracking
Krishnan, M. Ajay
Raja, V. S.
CORROSION SCIENCE, 2016, 109 : 94 - 100
[30] Environmentally assisted cracking of low alloy bainitic steel in high temperature water environment
Matocha, K
Wozniak, J
Klimsza, A
Siegl, J
RISK, ECONOMY AND SAFETY, FAILURE MINIMISATION AND ANALYSIS: FAILURES 98, 1998, : 317 - 323

← 1 2 3 4 5 →