Environmentally assisted degradation spinodal copper alloy C72900

被引：20

作者：

Johnsen, Roy ^{[1
]}

Lange, Torstein ^{[2
]}

Stenerud, Gaute ^{[1
]}

Olsen, Jim Stian ^{[1
,3
]}

机构：

[1] Norwegian Univ Sci & Technol, Trondheim, Norway

[2] SINTEF, Trondheim, Norway

[3] Aker Solut, Fornebu, Norway

来源：

CORROSION SCIENCE | 2018年 / 142卷

关键词：

Copper; Hydrogen embrittlement; Stress corrosion; Sulfide cracking; Cathodic protection; De-alloying; CU-15NI-8SN ALLOY; DISCONTINUOUS PRECIPITATION; DECOMPOSITION;

D O I：

10.1016/j.corsci.2018.06.031

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this work, a spinodal Copper alloy - C72900, was tested to investigate the resistance against environmentally assisted degradation. The material was tested according to ISO 15156-3 Level V in sour H2S solution and to cathodic polarization in simulated seawater with stressed samples. The results showed no indications of hydrogen stress cracking under cathodic polarization in seawater. However, cracks up to 3 mm deep were found on the samples exposed to sour H2S environment. Energy Dispersive Spectroscopy showed severe depletion of copper close to the cracks which is associated with selective corrosion. Stress corrosion cracking was the dominating crack mechanism in the ISO 15156-3 Level V test.

引用

页码：45 / 55

页数：11

共 50 条

[11] Threshold velocity for Environmentally-Assisted Cracking in low alloy steels
Wire, GL
Kandra, JT
PROCEEDINGS OF THE EIGHTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS - WATER REACTORS, VOLS 1 AND 2, 1997, : 932 - 940
[12] Model for environmentally assisted cracking of alloy 600 in PWR primary water
Lagerström, J
Ehrnstén, U
Saario, T
Hänninen, H
PROCEEDINGS OF THE EIGHTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS - WATER REACTORS, VOLS 1 AND 2, 1997, : 349 - 356
[13] Environmentally assisted small fatigue crack growth in 7017 aluminium alloy
Lu, ZJ
Evans, WJ
ADVANCES IN FRACTURE RESEARCH, VOLS 1-6, 1997, : 1459 - 1466
[14] THE ENVIRONMENTALLY ASSISTED FAILURE OF A CU-AG ALLOY IN AN AMINE ENVIRONMENT
SORENSEN, NR
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1984, 131 (08) : C303 - C303
[15] Failure avoidance - Environmentally assisted fracture of alloy 600-alloy 500 choke valve
Abusowa, K
El Shawesh, F
MATERIALS PERFORMANCE, 1999, 38 (06) : 78 - 80
[16] Evaluation of Microscopic Degradation of Copper and Copper Alloy by Electrical Resistivity Measurement
Kim, Chungseok
Nahm, Seunghoon
Hyun, Changyoung
JOURNAL OF THE KOREAN SOCIETY FOR NONDESTRUCTIVE TESTING, 2010, 30 (05) : 444 - 450
[17] Local Structure Study of spinodal decomposition in Copper-Nickel-Tin alloy using EXAFS
Poswal, A. K.
Basak, C. B.
Agrawal, Ankur
Bhattachryya, D.
Jha, S. N.
Sahoo, N. K.
61ST DAE-SOLID STATE PHYSICS SYMPOSIUM, 2017, 1832
[18] Modelling of environmentally assisted material degradation in the crack phase-field framework
Falkenberg, Rainer
PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART L-JOURNAL OF MATERIALS-DESIGN AND APPLICATIONS, 2019, 233 (01) : 5 - 12
[19] Environmentally Assisted Cracking Behavior of Alloy 182 Weld in Sulfuric Acid Solution
Tsai, W. -T.
Huang, C. -I.
Yang, C. -H.
CORROSION, 2009, 65 (01) : 15 - 23
[20] ENVIRONMENTALLY ASSISTED CRACKING OF ALLOY X-750 IN SIMULATED PWR COOLANT
SKELDON, P
SCOTT, PM
HURST, P
CORROSION, 1992, 48 (07) : 553 - 569

← 1 2 3 4 5 →