Microstructure and mechanical properties of the Si3N4/42CrMo steel joints brazed with Ag-Cu-Ti plus Mo composite filler

被引：76

作者：

He, Y. M. ^{[1
]}

Zhang, J. ^{[1
]}

Sun, Y. ^{[1
]}

Liu, C. F. ^{[1
]}

机构：

[1] Harbin Inst Technol, Sch Mat Sci & Engn, Harbin 150001, Peoples R China

来源：

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2010年 / 30卷 / 15期

关键词：

Si3N4; Joining; Ag-Cu-Ti plus Mo composite filler; Microstructure; Mechanical properties; SILICON-NITRIDE; STRENGTH; CERAMICS;

D O I：

10.1016/j.jeurceramsoc.2010.07.005

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The Si3N4 ceramic was joined to 42CrMo steel using Ag-Cu-Ti + Mo composite filler. Effect of Mo particles content on the microstructure and mechanical properties of the joints were investigated. Defect-free joints were received when the Si3N4/42CrMo steel joints were brazed with Ag-Cu-Ti + Mo composite filler. The results show that a continuous reaction layer which is composed of TiN and Ti5Si3 was formed near the Si3N4 ceramic. A double reaction layer which consists of Fe2Ti and FeTi was also formed adjacent to 42CrMo steel, with Fe2Ti being located near the steel. The central part of the joint is composed of Ag based solid solution, Cu based solid solution, Mo particles and some Cu-Ti intermetallic compounds. The maximal bending strength reached 587.3 MPa with 10 vol.% Mo particles in the joint, at which the joint strength was 414.3% higher than the average strength for the case without Mo particles addition. (C) 2010 Elsevier Ltd. All rights reserved.

引用

页码：3245 / 3251

页数：7

共 50 条

[21] y Microstructure and Mechanical Properties of the Joint between Si3N4 and Mo Brazed by Near-Eutectic Ag-Cu-In-Ti Filler Alloy
Zhao, Tong
Mo, Defeng
Shi, Xinmin
Sun, Wen
Li, Xue
Gong, Haimei
ADVANCED ENGINEERING MATERIALS, 2023, 25 (21)
[22] Microstructure and brazing mechanism of porous Si3N4/Invar joint brazed with Ag-Cu-Ti/Cu/Ag-Cu multi-layered filler
Zhang, J.
Liu, J. Y.
Wang, T. P.
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2018, 34 (04) : 713 - 719
[23] Microstructure and brazing mechanism of porous Si3N4/Invar joint brazed with Ag-Cu-Ti/Cu/Ag-Cu multi-layered filler
J.Zhang
J.Y.Liu
T.P.Wang
Journal of Materials Science & Technology, 2018, 34 (04) : 713 - 719
[24] Effect of holding time on microstructure and mechanical properties of SiC/SiC joints brazed by Ag-Cu-Ti + B4C composite filler
Dai, Xiangyu
Cao, Jian
Tian, Yingtao
Chen, Zhe
Song, Xiaoguo
Feng, Jicai
MATERIALS CHARACTERIZATION, 2016, 118 : 294 - 301
[25] Effect of Ti content on microstructure and strength of Si3N4/Si3N4 joints brazed with Cu-Pd-Ti filler metals
Liu, C. F.
Zhang, J.
Zhou, Y.
Meng, Q. C.
Naka, M.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 491 (1-2): : 483 - 487
[26] Microstructure and mechanical properties of transparent alumina and TiAl alloy joints brazed using Ag-Cu-Ti filler metal
Liu, X. P.
Zhang, L. X.
Sun, Z.
Feng, J. C.
VACUUM, 2018, 151 : 80 - 89
[27] Effect of Si3N4-particles addition in Ag-Cu-Ti filler alloy on Si3N4/TiAl brazed joint
Song, X. G.
Cao, J.
Wang, Y. F.
Feng, J. C.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (15): : 5135 - 5140
[28] Microstructure and Properties of Si3N4 Ceramics and 304 Stainless Steel Brazed Joint with Cu/Ag-Cu/Ti Laminated Filler Metal
Xu, X. P.
Liu, Q. M.
Xia, C. Z.
Zou, J. S.
HIGH TEMPERATURE MATERIALS AND PROCESSES, 2018, 37 (06) : 597 - 602
[29] Brazing Si3N4 ceramic with Ag-Cu-Ti+Mo composite filler
Zhang, J. (hitzhangjie@hit.edu.cn), 1600, Harbin Research Institute of Welding (34):
[30] Enhanced mechanical properties and thermal cycling stability of Al2O3-4J42 joints brazed using Ag-Cu-Ti/Cu/Ag-Cu composite filler
Zhu, Qianying
Li, Shenhou
Hu, Kangjia
Liang, Xuewei
Cai, Yangyang
Liu, Zheng
Zhang, Yong
CERAMICS INTERNATIONAL, 2021, 47 (21) : 30247 - 30255

← 1 2 3 4 5 →