Microstructure and mechanical properties of the Si3N4/42CrMo steel joints brazed with Ag-Cu-Ti plus Mo composite filler

被引：76
|
作者：
He, Y. M. [1 ]
Zhang, J. [1 ]
Sun, Y. [1 ]
Liu, C. F. [1 ]
机构：
[1] Harbin Inst Technol, Sch Mat Sci & Engn, Harbin 150001, Peoples R China
来源：
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2010年 / 30卷 / 15期
关键词：
Si3N4; Joining; Ag-Cu-Ti plus Mo composite filler; Microstructure; Mechanical properties; SILICON-NITRIDE; STRENGTH; CERAMICS;
D O I：
10.1016/j.jeurceramsoc.2010.07.005
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The Si3N4 ceramic was joined to 42CrMo steel using Ag-Cu-Ti + Mo composite filler. Effect of Mo particles content on the microstructure and mechanical properties of the joints were investigated. Defect-free joints were received when the Si3N4/42CrMo steel joints were brazed with Ag-Cu-Ti + Mo composite filler. The results show that a continuous reaction layer which is composed of TiN and Ti5Si3 was formed near the Si3N4 ceramic. A double reaction layer which consists of Fe2Ti and FeTi was also formed adjacent to 42CrMo steel, with Fe2Ti being located near the steel. The central part of the joint is composed of Ag based solid solution, Cu based solid solution, Mo particles and some Cu-Ti intermetallic compounds. The maximal bending strength reached 587.3 MPa with 10 vol.% Mo particles in the joint, at which the joint strength was 414.3% higher than the average strength for the case without Mo particles addition. (C) 2010 Elsevier Ltd. All rights reserved.
引用
收藏
页码：3245 / 3251
页数：7
相关论文
共 50 条
  • [31] Brazing Si3N4 Ceramic to Molybdenum Using an Ag-Cu-Ti Filler
    Zhao, T.
    Mo, D. F.
    Yu, L. Q.
    Wang, Y. Y.
    Li, J.
    Li, X.
    Liu, D. F.
    Wang, X. K.
    Gong, H. M.
    WELDING JOURNAL, 2021, 100 (06) : 206S - 212S
  • [32] The impact of TiC particle addition to Ag-Cu-Ti filler material on the microstructure and mechanical properties of AlN ceramic/Cu brazed joints
    Qie, Lutong
    Wang, Tao
    Yu, Zhanlong
    Guo, Weibing
    Chen, Xiaoguang
    WELDING IN THE WORLD, 2024,
  • [33] Properties and fracture processes of Si3N4/Si3N4 joints brazed using Cu-Zn-Ti filler alloy
    Zhang, J
    Naka, M
    Fang, HY
    Zhou, Y
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2004, 9 (02) : 158 - 162
  • [34] Comparative study on microstructure and strength of TiAl/steel joints brazed with Ag-Cu-Ti and Ag-Cu-Zn filler metals
    Liu, HJ
    Feng, JC
    NEW FRONTIERS OF PROCESSING AND ENGINEERING IN ADVANCED MATERIALS, 2005, 502 : 467 - 472
  • [35] Microstructure and mechanical property of Zr-4 alloys brazed with Ag-Cu-Ti filler metal
    Bai, Yujie
    Wang, Yao
    Liu, Yi
    Li, Yuanxing
    INTERNATIONAL JOURNAL OF MODERN PHYSICS B, 2024,
  • [36] Microstructure and mechanical properties of Al2O3 ceramic and TiAl alloy joints brazed with Ag-Cu-Ti filler metal
    Niu, G. B.
    Wang, D. P.
    Yang, Z. W.
    Wang, Y.
    CERAMICS INTERNATIONAL, 2016, 42 (06) : 6924 - 6934
  • [37] Reaction Layer Microstructure of SiC/SiC Joints Brazed by Ag-Cu-Ti Filler Metal
    Liu, Yan
    Huang, Zhengren
    Liu, Xiujian
    HIGH-PERFORMANCE CERAMICS VI, 2010, 434-435 : 202 - 204
  • [38] Interfacial microstructure of the Si3N4/Si3N4 joint brazed with Cu-Pd-Ti filler alloy
    Zhang, J.
    Zhou, Y.
    Naka, M.
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2006, 26 (15) : 3459 - 3466
  • [39] Ag effect on microstructures and strength of Si3N4/Si3N4 joint brazed with Cu-Ag-Ti filler metals
    Tamai, F
    Naka, M
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1996, 15 (15) : 1353 - 1354
  • [40] Microstructure and mechanical properties of Ti2AlNb alloy and C/C composite joints brazed with Ag-Cu-Zn and Ag-Cu-Zn/Cu/Ag-Cu-Ti filler metals
    Hao, Zhitao
    Wang, Dongpo
    Yang, Zhenwen
    Wang, Ying
    ARCHIVES OF CIVIL AND MECHANICAL ENGINEERING, 2019, 19 (04) : 1083 - 1094
12345