EFFECT OF Ti CONTENT ON THE MICROSTRUCTURE AND PROPERTIES OF Si3n4/Si3N4 JOINT BRAZED USING Cu-Zn-Ti ALLOY

被引：0
|
作者：
M. Naka
J. Zhang
H. Y. Fang (1.Joining and Welding Research Institute
机构：
来源：
ActaMetallurgicaSinica(EnglishLetters) | 2000年 / 01期
关键词：
Si3N4; ceramic; Ti; brazing; microstructure; mechanical property;
D O I：
暂无
中图分类号：
TG457 [各种金属材料和构件的焊接];
学科分类号：
摘要：
St3N4 ceramic was brazed using a filler of Cu - Zn - Ti alloy under the brazing condition of 1223K and 1.8ks. When the Ti content in the alloy is 20% at., the average shear strength of the joint is 265MPa. By using EPMA and XRD analysis, the metallurgical behavior of the interface between the filler alloy and Si3N4 matrix was studied,which affected the joint strength.It was found that with in- creasing Ti content from 5% to 20%at., the thickness of the brazing seam decreases and the amount of the reactant(Ti5Si3, TiN and Ti2N etc. ) increases,resulting in an obvious increase of the shear strength of the joint.
引用
收藏
页码：23 / 27
页数：5
相关论文
共 50 条
  • [31] Microstructure and mechanical properties of invar alloy and Si3N4 ceramic brazed joints
    Wang, Ying
    Yang, Zhenwen
    Zhang, Lixia
    Feng, Jicai
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2015, 44 (02): : 341 - 343
  • [32] Microstructure and Mechanical Properties of Invar Alloy and Si3N4 Ceramic Brazed Joints
    Wang Ying
    Yang Zhenwen
    Zhang Lixia
    Feng Jicai
    RARE METAL MATERIALS AND ENGINEERING, 2015, 44 (02) : 339 - 343
  • [33] Tribological properties of Ti/Si3N4 implanted by N ions
    Tian, Jun
    Yang, Xiaohong
    Chen, Yufeng
    Wang, Qizu
    Xue, Qunji
    Kuei Suan Jen Hsueh Pao/ Journal of the Chinese Ceramic Society, 26 (02): : 206 - 209
  • [34] y Microstructure and Mechanical Properties of the Joint between Si3N4 and Mo Brazed by Near-Eutectic Ag-Cu-In-Ti Filler Alloy
    Zhao, Tong
    Mo, Defeng
    Shi, Xinmin
    Sun, Wen
    Li, Xue
    Gong, Haimei
    ADVANCED ENGINEERING MATERIALS, 2023, 25 (21)
  • [35] Microstructure and Properties of Si3N4 Ceramics and 304 Stainless Steel Brazed Joint with Cu/Ag-Cu/Ti Laminated Filler Metal
    Xu, X. P.
    Liu, Q. M.
    Xia, C. Z.
    Zou, J. S.
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2018, 37 (06) : 597 - 602
  • [36] Si3N4/Ti/Cu/Ni/Cu/Ti/Si3N4二次部分瞬间液相连接强度
    邹家生
    许志荣
    初亚杰
    赵其章
    焊接学报, 2005, (02) : 41 - 44+7
  • [37] Microstructure and strength of Si3N4 joint brazed with Ti40Zr25Ni15Cu20 amorphous brazing alloy
    Provincial Key Laboratory of Advanced Welding Technology, Jiangsu University of Science and Technology, Zhenjiang 212003, China
    Hanjie Xuebao, 2007, 3 (45-48):
  • [38] Microstructure evolution of the Si3N4/Si3N4 joints brazed using Au-Ni-V filler alloys with different V content
    Sun, Y.
    Zhang, J.
    Zhang, H. W.
    Fan, G. H.
    He, Y. M.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2011, 509 (33) : 8407 - 8412
  • [39] Microstructure and Selected Properties of Si3N4
    Gabrisova, Zuzana
    Svec, Pavol
    Brusilova, Alena
    MANUFACTURING TECHNOLOGY, 2020, 20 (03): : 293 - 299
  • [40] Effect of β-Si3N4 seeds on microstructure and properties of porous Si3N4 ceramics prepared by gelcasting using DMAA system
    Yin, Shuang
    Pan, Limei
    Liu, Yun
    Wang, Yang
    Qiu, Tai
    Yang, Jian
    CERAMICS INTERNATIONAL, 2020, 46 (04) : 4924 - 4932
12345