EFFECT OF Ti CONTENT ON THE MICROSTRUCTURE AND PROPERTIES OF Si3n4/Si3N4 JOINT BRAZED USING Cu-Zn-Ti ALLOY

被引：0
|
作者：
M. Naka
J. Zhang
H. Y. Fang (1.Joining and Welding Research Institute
机构：
来源：
ActaMetallurgicaSinica(EnglishLetters) | 2000年 / 01期
关键词：
Si3N4; ceramic; Ti; brazing; microstructure; mechanical property;
D O I：
暂无
中图分类号：
TG457 [各种金属材料和构件的焊接];
学科分类号：
摘要：
St3N4 ceramic was brazed using a filler of Cu - Zn - Ti alloy under the brazing condition of 1223K and 1.8ks. When the Ti content in the alloy is 20% at., the average shear strength of the joint is 265MPa. By using EPMA and XRD analysis, the metallurgical behavior of the interface between the filler alloy and Si3N4 matrix was studied,which affected the joint strength.It was found that with in- creasing Ti content from 5% to 20%at., the thickness of the brazing seam decreases and the amount of the reactant(Ti5Si3, TiN and Ti2N etc. ) increases,resulting in an obvious increase of the shear strength of the joint.
引用
收藏
页码：23 / 27
页数：5
相关论文
共 50 条
  • [21] Interfacial microstructure of Si3N4/Si3N4 joint brazed using Au–Ni–V filler alloy
    J. Zhang
    Y. Sun
    C. F. Liu
    H. W. Zhang
    Journal of Materials Science, 2010, 45 : 2188 - 2193
  • [22] Microstructure and properties of the Si3N4/Si3N4 brazing joint
    Zhang, J
    Naka, N
    Zhou, Y
    Lei, TQ
    MECHANICS AND MATERIAL ENGINEERING FOR SCIENCE AND EXPERIMENTS, 2001, : 222 - 225
  • [23] Effect of Si3N4-particles addition in Ag-Cu-Ti filler alloy on Si3N4/TiAl brazed joint
    Song, X. G.
    Cao, J.
    Wang, Y. F.
    Feng, J. C.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (15): : 5135 - 5140
  • [24] Interfacial microstructure of Si3N4/Si3N4 joint brazed using Au-Ni-V filler alloy
    Zhang, J.
    Sun, Y.
    Liu, C. F.
    Zhang, H. W.
    JOURNAL OF MATERIALS SCIENCE, 2010, 45 (08) : 2188 - 2193
  • [25] Microstructure and mechanical properties of an Si3N4/Si3N4 joint brazed with Au-Ni-Pd-V filler alloy
    Sun, Y.
    Zhang, J.
    Geng, Y. P.
    Ikeuchi, K.
    Shibayanagi, T.
    SCRIPTA MATERIALIA, 2011, 64 (05) : 414 - 417
  • [26] Effect of brazing temperature on microstructure and mechanical properties of Si3N4/Si3N4 joints brazed with Ag-Cu-Ti plus Mo composite filler
    He, Y. M.
    Zhang, J.
    Wang, X.
    Sun, Y.
    JOURNAL OF MATERIALS SCIENCE, 2011, 46 (08) : 2796 - 2804
  • [27] Study on interfacial structure and strength of Si3N4/Ti/Cu/Ti/Si3N4 PTLP bonding
    邹家生
    蒋志国
    许志荣
    陈广
    China Welding, 2006, (01) : 11 - 15
  • [28] Study on interfacial structure and strength of Si3N4/Ti/Cu/Ti/Si3N4 PTLP bonding
    Department of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094, China
    不详
    China Weld Eng Ed, 2006, 1 (11-15):
  • [29] The influence of Ti: Si3N4 ratio on the microstructure evolution of Ti-Si3N4 reaction in Cu melts
    Zhang, Xiao
    Ding, Haimin
    Liu, Qing
    Wang, Jinfeng
    Wang, Xianlong
    Jie, Jinchuan
    CERAMICS INTERNATIONAL, 2022, 48 (18) : 25798 - 25807
  • [30] Effect of brazing temperature on interfacial microstructure and properties of Ti60/Si3N4 brazed joints
    Hu T.
    Lei Y.
    Hu S.
    Song X.
    Wang C.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2018, 39 (08): : 28 - 31and37
12345