EFFECT OF Ti CONTENT ON THE MICROSTRUCTURE AND PROPERTIES OF Si3n4/Si3N4 JOINT BRAZED USING Cu-Zn-Ti ALLOY

被引：0

作者：

M. Naka

J. Zhang

H. Y. Fang (1.Joining and Welding Research Institute

机构：

来源：

ActaMetallurgicaSinica(EnglishLetters) | 2000年 / 01期

关键词：

Si3N4; ceramic; Ti; brazing; microstructure; mechanical property;

D O I：

暂无

中图分类号：

TG457 [各种金属材料和构件的焊接];

学科分类号：

摘要：

St3N4 ceramic was brazed using a filler of Cu - Zn - Ti alloy under the brazing condition of 1223K and 1.8ks. When the Ti content in the alloy is 20% at., the average shear strength of the joint is 265MPa. By using EPMA and XRD analysis, the metallurgical behavior of the interface between the filler alloy and Si3N4 matrix was studied,which affected the joint strength.It was found that with in- creasing Ti content from 5% to 20%at., the thickness of the brazing seam decreases and the amount of the reactant(Ti5Si3, TiN and Ti2N etc. ) increases,resulting in an obvious increase of the shear strength of the joint.

引用

页码：23 / 27

页数：5

共 50 条

[1] Effect of Ti content on the microstructure and properties of Si3N4/Si3N4 joint brazed using Cu-Zn-Ti alloy
Naka, M.
Zhang, J
Fang, H.Y.
Acta Metallurgica Sinica (English Letters), 2000, 13 (01) : 23 - 27
[2] Effect of bonding condition on microstructure and properties of the Si3N4/Si3N4 joint brazed using Cu-Zn-Ti filler alloy
Zhang, J
Fang, HY
Zhou, Y
Naka, M
COMPOSITE MATERIALS III, 2003, 249 : 255 - 260
[3] Effect of bonding parameters on microstructure and properties of Si3N4/Si3N4 joint brazed by Cu-Zn-Ti filler alloy
张杰
周玉
Transactions of Nonferrous Metals Society of China, 2005, (03) : 497 - 503
[4] Effect of bonding parameters on microstructure and properties of Si3N4/Si3N4 joint brazed by Cu-Zn-Ti filler alloy
Zhang, J
Naka, M
Zhou, Y
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2005, 15 (03) : 497 - 503
[5] Interfacial microstructure of Si3N4/Si3N4 brazing joint with Cu-Zn-Ti filler alloy
Zhang, J.
Zhang, X. M.
Zhou, Y.
Naka, M.
Svetlana, Atroshenko
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 495 (1-2): : 271 - 275
[6] Properties and fracture processes of Si3N4/Si3N4 joints brazed using Cu-Zn-Ti filler alloy
Zhang, J
Naka, M
Fang, HY
Zhou, Y
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2004, 9 (02) : 158 - 162
[7] A TEM analysis of the Si3N4/Si3N4 joint brazed with a Cu-Zn-Ti filler metal
J. Zhang
C. F. Liu
M. Naka
Q.C. Meng
Y. Zhou
Journal of Materials Science, 2004, 39 : 4587 - 4591
[8] Interfacial reaction and growth behavior of reaction layer of Si3N4/Si3N4 joint brazed by Cu-Zn-Ti filler alloy
Zhang, J
Zhou, Y
Naka, M
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2005, 15 : 261 - 265
[9] A TEM analysis of the Si3N4/Si3N4 joint with a Cu-Zn-Ti filler metal
Zhang, J
Liu, CF
Naka, M
Meng, QC
Zhou, Y
JOURNAL OF MATERIALS SCIENCE, 2004, 39 (14) : 4587 - 4591
[10] Interfacial microstructure of the Si3N4/Si3N4 joint brazed with Cu-Pd-Ti filler alloy
Zhang, J.
Zhou, Y.
Naka, M.
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2006, 26 (15) : 3459 - 3466

← 1 2 3 4 5 →