Effect of Squeeze Cast Process Parameters on Fluidity of Hypereutectic Al-Si Alloy

被引：0
|
作者：
Jong-Kyu Baek
Hae-Wook Kwon
机构：
[1] Korea
[2] School of-Materials Science and Engineering Yeungnam University Gyeongsan 712-749
来源：
Journal of Materials Science & Technology | 2008年 / 01期
关键词：
Squeeze casting; Al-alloy; Fluidity; Melt treatment;
D O I：
暂无
中图分类号：
TG249.2 [压力铸造];
学科分类号：
摘要：
The effects of processing variables on the fluidity of hypereutectic Al-Si alloy melt during squeeze casting were investigated.The maximum fluidity of Al-16.0%Si alloy during squeeze casting was obtained under the applied pressure of 30 MPa.The fluidity increased with superheat.The fluidity increased with silicon content in the range from 12.0% to 20.0%.That was decreased respectively by eutectic modification and primary silicon refinement.
引用
收藏
页码：7 / 11
页数：5
相关论文
共 50 条
  • [31] Effect of Nd on primary silicon and eutectic silicon in hypereutectic Al-Si alloy
    Xu, C. L.
    Jiang, Q. C.
    Yang, Y. F.
    Wang, H. Y.
    Wang, J. G.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2006, 422 (1-2) : L1 - L4
  • [32] Refinement of primary Si in hypereutectic Al-Si alloy by electromagnetic stirring
    Lu, Dehong
    Jiang, Yehua
    Guan, Guisheng
    Zhou, Rongfeng
    Li, Zhenhua
    Zhou, Rong
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2007, 189 (1-3) : 13 - 18
  • [33] Effect of process parameters on porosity defects in Al-Si alloy hot rolling
    Zhao, Yanling
    Jin, Yuan
    Bao, Yudong
    PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART B-JOURNAL OF ENGINEERING MANUFACTURE, 2023, 237 (05) : 770 - 778
  • [34] Effects of ZnS modification on primary Si in hypereutectic Al-Si alloy
    Cheng-dong Li
    Chuan-hao Sun
    Wen-qiang Si
    Mei Zhao
    Man-man Lu
    Lei Zhang
    China Foundry, 2017, 14 : 93 - 97
  • [35] Effects of cooling rate on primary Si in hypereutectic Al-Si alloy
    Kunming University of Science and Technology, Kunming 650093, China
    Tezhong Zhuzao Ji Youse Hejin, 2006, 1 (34-35):
  • [36] Effects of ZnS modification on primary Si in hypereutectic Al-Si alloy
    Cheng-dong Li
    Chuan-hao Sun
    Wen-qiang Si
    Mei Zhao
    Man-man Lu
    Lei Zhang
    China Foundry, 2017, 14 (02) : 93 - 97
  • [37] THE EFFECT OF CASTING PARAMETERS ON THE MODIFICATION PROCESS OF A COMMERCIAL HYPOEUTECTIC AL-SI ALLOY
    HAFIZ, MF
    FATHALLA, NK
    MOSHREF, SB
    ZEITSCHRIFT FUR METALLKUNDE, 1990, 81 (01): : 70 - 75
  • [38] Characteristics and microstructure of hypereutectic Al-Si alloy powder by ultrasonic gas atomization process
    Xie, Zhuangde
    Sun, Jianfei
    Shen, Jun
    Zhou, Bide
    Su, Zhijun
    Le, Hongsheng
    Fenmo Yejin Jishu/Powder Metallurgy Technology, 2001, 19 (06): : 331 - 334
  • [39] Effects of ZnS modification on primary Si in hypereutectic Al-Si alloy
    Li, Cheng-dong
    Sun, Chuan-hao
    Si, Wen-qiang
    Zhao, Mei
    Lu, Man-man
    Zhang, Lei
    CHINA FOUNDRY, 2017, 14 (02) : 93 - 97
  • [40] Characteristics and microstructure of a hypereutectic Al-Si alloy powder by ultrasonic gas atomization process
    Shen, J.
    Xie, Z.D.
    Zhou, B.D.
    Li, Q.C.
    Su, Z.J.
    Le, H.S.
    2001, Chinese Society of Metals (17):
12345