Scavenging of the Metal Bath with Inert Gases during the Top-Blown Oxygen Converter Process.

被引：0

作者：

Bialowas, Wieslaw ^{[1
]}

Michaliszyn, Andrej ^{[1
]}

Dziarmagowski, Marek ^{[1
]}

机构：

[1] Akad Gorniczo-Hutnicza, Cracow, Pol, Akad Gorniczo-Hutnicza, Cracow, Pol

来源：

Hutnik Warszawa | 1985年 / 52卷 / 09期

关键词：

GASES; INERT; -; Applications; THERMODYNAMICS; Optimization;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

A literature review of new technologies based on surveying the metal bath with inert gases is presented. It is shown that scavenging the metal bath with inert gases during the LD process yields the following advantages: an increase in the metal yield, a decrease in spattering from the converter, improvement of the slag formation conditions and low carbon contents in steel in the final stage of the process.

引用

页码：290 / 292

共 45 条

[41] ADJUSTMENT OF CARBON AND OXYGEN CONTENTS OF THE BATH IN THE BASIC OXYGEN STEELMAKING PROCESS WITH BOTTOM STIRRING .2. CHANGE OF C-CONTENT AND O-CONTENT DURING STIRRING WITH INERT-GAS
SCHURMANN, E
HOFFKEN, R
ZITZEN, W
ULLRICH, W
SCHICKS, H
STAHL UND EISEN, 1992, 112 (02): : 71 - 76
[42] A Thermodynamic Model of Phosphate Capacity for CaO-SiO2-MgO-FeO-Fe2O3-MnO-Al2O3-P2O5 Slags Equilibrated with Molten Steel during a Top–Bottom Combined Blown Converter Steelmaking Process Based on the Ion and Molecule Coexistence Theory
Xue-Min Yang
Cheng-Bin Shi
Meng Zhang
Jian-Ping Duan
Jian Zhang
Metallurgical and Materials Transactions B, 2011, 42 : 951 - 977
[43] A Thermodynamic Model of Phosphorus Distribution Ratio between CaO-SiO2-MgO-FeO-Fe2O3-MnO-Al2O3-P2O5 Slags and Molten Steel during a Top–Bottom Combined Blown Converter Steelmaking Process Based on the Ion and Molecule Coexistence Theory
Xue-Min Yang
Jian-Ping Duan
Cheng-Bin Shi
Meng Zhang
Yong-Liang Zhang
Jian-Chang Wang
Metallurgical and Materials Transactions B, 2011, 42 : 738 - 770
[44] A Thermodynamic Model of Phosphate Capacity for CaO-SiO2-MgO-FeO-Fe2O3-MnO-Al2O3-P2O5 Slags Equilibrated with Molten Steel during a Top-Bottom Combined Blown Converter Steelmaking Process Based on the Ion and Molecule Coexistence Theory
Yang, Xue-Min
Shi, Cheng-Bin
Zhang, Meng
Duan, Jian-Ping
Zhang, Jian
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2011, 42 (05): : 951 - 977
[45] A Thermodynamic Model of Phosphorus Distribution Ratio between CaO-SiO2-MgO-FeO-Fe2O3-MnO-Al2O3-P2O5 Slags and Molten Steel during a Top-Bottom Combined Blown Converter Steelmaking Process Based on the Ion and Molecule Coexistence Theory
Yang, Xue-Min
Duan, Jian-Ping
Shi, Cheng-Bin
Zhang, Meng
Zhang, Yong-Liang
Wang, Jian-Chang
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2011, 42 (04): : 738 - 770

← 1 2 3 4 5 →