Effect of alloy composition on heat resistance and castability of Mg-Al2Ca(Mg) quasi-binary alloys

被引：1

作者：

Kawabata H. ^{[1
]}

Nishino N. ^{[1
]}

Aikawa T. ^{[2
]}

Ohtake K. ^{[3
]}

Genma Y. ^{[3
]}

机构：

[1] Toyota Central R and D Labs. Inc., Nagakute, Nagakute-cho, Aichi-gun, Aichi 480-1192

[2] Aisin Seiki Co., Ltd., Kariya-shi, Aichi

[3] Toyota Motor Corporation, Toyota-shi, Aichi

来源：

Keikinzoku/Journal of Japan Institute of Light Metals | 2010年 / 60卷 / 11期

关键词：

Castability; Diecasting; Heat resistance; Magnesium alloy;

D O I：

10.2464/jilm.60.596

中图分类号：

学科分类号：

摘要：

The effects of the amount of the Al2Ca(Mg) compound on heat resistance and castability of the Mg-Al2Ca(Mg) quasi-binary alloys, the composition ratio of aluminum and calcium of which was 2:1, were investigated. The heat resistance of the Mg-Al2Ca(Mg) quasi-binary alloys was improved by the covering of α-Mg grain boundaries with the Al2Ca(Mg) compound, and more improved by increasing of the amount of the Al2Ca(Mg) compound. The Mg-Al2Ca(Mg) quasi-binary alloys, the compositions of which were close to eutectic one, showed the alloy solidification of the skin-formation type. The duration of the transferred pressure of those molten alloys was long, and the alloys showed the high transfer ability of alloy solidification. It improved the heat resistance and the castability of the Mg-Al2Ca(Mg) quasi-binary alloys for the compositions of aluminum and calcium to be closer to eutectic.

引用

页码：596 / 601

页数：5

共 50 条

[31] The effect of Ca and Mn addition on ignition temperature, castability, and electrochemical properties of Mg-alloy by casting
Kim, Hye-Sung
Kim, Tae-Gyu
HEAT TREATMENT OF MATERIALS, 2006, 118 (485-490): : 485 - +
[32] Comparison on Hot Tearing Behavior of Binary Mg-Al, Mg-Y, Mg-Gd, Mg-Zn, and Mg-Ca Alloys
Song, Jiangfeng
Zhao, Hua
Liao, Jinge
Jiang, Bin
Zhang, Ang
Huang, Yuanding
Kainer, Karl Ulrich
Hort, Norbert
Pan, Fusheng
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2022, 53 (08): : 2986 - 3001
[33] Structure, phase composition, and strengthening of cast Al–Ca–Mg–Sc alloys
N. A. Belov
E. A. Naumova
T. A. Bazlova
E. V. Alekseeva
The Physics of Metals and Metallography, 2016, 117 : 188 - 194
[34] Effect of Al addition and heat treatment on the microstructures and corrosion resistance of Mg-Cu alloys
Wang, X. W.
Wang, W.
Chen, W.
Chen, D. M.
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2022, 98 : 219 - 232
[35] Effect of Al Composition on the Corrosion Resistance of Mg-14 mass% Li System Alloy
Morishige, Taiki
Obata, Yutaro
Goto, Takayuki
Fukagawa, Tomoki
Nakamura, Eiji
Takenaka, Toshihide
MATERIALS TRANSACTIONS, 2016, 57 (10) : 1853 - 1856
[36] Effect of Al addition and heat treatment on the microstructures and corrosion resistance of Mg-Cu alloys
X.W.Wang
W.Wang
W.Chen
D.M.Chen
JournalofMaterialsScience&Technology, 2022, 98 (03) : 219 - 232
[37] Influence of Cu/Mg ratio and content on heat-resistance of Al-Cu-Mg alloys
Yang, Huabing
Liu, Yunteng
Li, Ying
Zhang, Suqing
Wu, Jianhua
Yu, Huan
Liu, Hongtao
Ma, Baichang
Zhuang, Haihua
Feng, Xuansheng
Zhang, Peng
Zhou, Jixue
Liu, Xiangfa
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 29 : 1040 - 1051
[38] Effect of Mg composition on sintering behaviors and mechanical properties of Al-Cu-Mg alloy
Oh, Min Chul
Ahn, Byungmin
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2014, 24 : S53 - S58
[39] Coherency evaluation of a-Mg/C15-Al2Ca interface for a Mg-Al-Ca alloy
Hisazawa, Hiromu
Kashiwase, Sakiko
Terada, Yoshihiro
Keikinzoku/Journal of Japan Institute of Light Metals, 2021, 71 (02): : 127 - 129
[40] Effect of Heat Treatment on Corrosion Resistance of Zn-Mg-Al Alloy Coated Steel
Sohn, Il Ryoung
Kim, Tae Chul
Kim, Sung Ju
Kim, Myung Soo
Kim, Jong Sang
Lim, Woo Jin
Bae, Seong Mo
Shin, Su Hee
Paik, Doo Jin
CORROSION SCIENCE AND TECHNOLOGY-KOREA, 2024, 23 (04): : 283 - 288

← 1 2 3 4 5 →