Low-Temperature Pressureless Sintering Properties of Submicron Silver Pastes

被引：0
|
作者：
Xin, Li [1 ]
Zhiwei, Wang [1 ]
机构：
[1] School of Materials Science and Engineering, Tianjin University, Tianjin,300350, China
来源：
Tianjin Daxue Xuebao (Ziran Kexue yu Gongcheng Jishu Ban)/Journal of Tianjin University Science and Technology | 2024年 / 57卷 / 09期
关键词：
Sintered silver pastes show excellent properties such as high thermal conductivity; high electrical conductivity; low elastic modulus; and high reliability; allowing them to maximize the potential of SiC and GaN devices; thus; these pastes have broad application prospects. To reduce the preparation cost and improve the sintering performance of the silver pastes; three types of sintered silver pastes were prepared using two types of submicron silver particles:spherical and flaky. The sintering properties of submicron silver particles with different morphologies and mixed particles were examined by analyzing the electrical resistivity; shear strength; and microscopic morphology of the silver pastes sintered at 200 —250 ℃ without pressure. The silver paste prepared from spherical silver particles showed a high shear strength of 52.4 MPa after sintering at 250 ℃; and its electrical resistivity was only 6.28× 10-8 Ω·m. The silver paste prepared from silver flakes showed a low shear strength and high electrical resistivity after sintering. When the silver paste prepared from silver flakes was sintered at 250 ℃; the shear strength was 21.5 MPa; and the electrical resistivity was 15.54×10-8 Ω·m; which was attributed to the large radial size of the silver flakes; low tap density; and sintering structure of the silver flakes stacked in layers. The silver paste with mixed particles showed potential for sintering at 200 ℃; with a shear strength of 28.2 MPa and electrical resistivity of 7.77×10-8 Ω·m; which was attributed to the silver flakes. The submicron silver flakes promoted faster evaporation of the selected organic components and a higher initial packing density of the mixed particles. These results contributed to the mature and stable preparation of submicron silver pastes and provided a new approach for developing high-performance silver pastes with low-temperature pressure-less sintering properties. © 2024 Tianjin University. All rights reserved;
D O I：
10.11784/tdxbz202305036
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：974 / 981
相关论文
共 50 条
  • [31] Pressureless Sintering and Properties of Silver Film for Electromagnetic Induction Heating
    Luo Guoqiang
    Wang Chunsheng
    Hu Jianian
    Chen Changlian
    Yi, Sun
    Li Meijuan
    Wang Chuanbin
    Qiang, Shen
    RARE METAL MATERIALS AND ENGINEERING, 2021, 50 (05) : 1694 - 1698
  • [32] Low-temperature sintering of highly conductive silver ink for flexible electronics
    Bhat, Kiesar Sideeq
    Ahmad, Rafiq
    Wang, Yousheng
    Hahn, Yoon-Bong
    JOURNAL OF MATERIALS CHEMISTRY C, 2016, 4 (36) : 8522 - 8527
  • [33] Preparation of Silver Nanoparticle with Different Particle Sizes for Low-Temperature Sintering
    Hsu, Steve Lien-Chung
    Wu, Rong-Tarng
    NANOTECHNOLOGY AND BIOSENSORS, 2011, : 55 - 58
  • [34] Waste Form of Silver Iodide (AgI) with Low-Temperature Sintering Glasses
    Yang, Jae Hwan
    Shin, Jin Myeong
    Park, Jang Jin
    Park, Geun Il
    SEPARATION SCIENCE AND TECHNOLOGY, 2014, 49 (02) : 298 - 304
  • [35] Low-Temperature Pressureless Sintering of Sr- and Mg-Doped Lanthanum Gallate Ceramics by Sintering Atmosphere Control
    Chang, Jaemyung
    Lee, Hae-Weon
    Kang, Suk-Joong L.
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2009, 92 (04) : 927 - 930
  • [36] Low-temperature and pressureless sintering technology for high-performance and high-temperature interconnection of semiconductor devices
    Lu, Guo-Quan
    Calata, Jesus N.
    Lei, Guangyin
    Chen, Xu
    EUROSIME 2007: THERMAL, MECHANICAL AND MULTI-PHYSICS SIMULATION AND EXPERIMENTS IN MICRO-ELECTRONICS AND MICRO-SYSTEMS, PROCEEDINGS, 2007, : 609 - +
  • [37] Silver oxide-mediated synergistic enhancement of conductivity and adhesion in low-temperature cured silver pastes
    Guo, Yi-Chen
    Liao, Xiao-Gang
    Wu, Qi
    Hao, Yu-Xuan
    Wang, Zi-Hao
    Zhang, Wen-Yan
    Wang, Yao-Yu
    CRYSTENGCOMM, 2025, 27 (14) : 2166 - 2174
  • [38] Preparation and Low Temperature Sintering of Silver Nanoparticles Based Pastes for Power Semiconductor Device Interaction
    Shen, Qinchen
    Liang, Xianwen
    Li, Gang
    Zhu, Pengli
    Zhao, Tao
    Sun, Rong
    Fan, Yanfang
    2020 21ST INTERNATIONAL CONFERENCE ON ELECTRONIC PACKAGING TECHNOLOGY (ICEPT), 2020,
  • [39] Pressureless Silver Sintering in Power Application
    Pietrikova, Alena
    Girasek, Tomas
    Durisin, Juraj
    Saksl, Karel
    2018 INTERNATIONAL CONFERENCE ON DIAGNOSTICS IN ELECTRICAL ENGINEERING (DIAGNOSTIKA), 2018,
  • [40] Development of Low-temperature Sintering Nano-Ag Pastes Using Lowering Modulus Technologies
    Sasaki, Koji
    Mizumura, Noritsuka
    2017 IEEE 17TH INTERNATIONAL CONFERENCE ON NANOTECHNOLOGY (IEEE-NANO), 2017, : 897 - 902
12345