Low-Temperature Pressureless Sintering Properties of Submicron Silver Pastes

被引：0
|
作者：
Xin, Li [1 ]
Zhiwei, Wang [1 ]
机构：
[1] School of Materials Science and Engineering, Tianjin University, Tianjin,300350, China
来源：
Tianjin Daxue Xuebao (Ziran Kexue yu Gongcheng Jishu Ban)/Journal of Tianjin University Science and Technology | 2024年 / 57卷 / 09期
关键词：
Sintered silver pastes show excellent properties such as high thermal conductivity; high electrical conductivity; low elastic modulus; and high reliability; allowing them to maximize the potential of SiC and GaN devices; thus; these pastes have broad application prospects. To reduce the preparation cost and improve the sintering performance of the silver pastes; three types of sintered silver pastes were prepared using two types of submicron silver particles:spherical and flaky. The sintering properties of submicron silver particles with different morphologies and mixed particles were examined by analyzing the electrical resistivity; shear strength; and microscopic morphology of the silver pastes sintered at 200 —250 ℃ without pressure. The silver paste prepared from spherical silver particles showed a high shear strength of 52.4 MPa after sintering at 250 ℃; and its electrical resistivity was only 6.28× 10-8 Ω·m. The silver paste prepared from silver flakes showed a low shear strength and high electrical resistivity after sintering. When the silver paste prepared from silver flakes was sintered at 250 ℃; the shear strength was 21.5 MPa; and the electrical resistivity was 15.54×10-8 Ω·m; which was attributed to the large radial size of the silver flakes; low tap density; and sintering structure of the silver flakes stacked in layers. The silver paste with mixed particles showed potential for sintering at 200 ℃; with a shear strength of 28.2 MPa and electrical resistivity of 7.77×10-8 Ω·m; which was attributed to the silver flakes. The submicron silver flakes promoted faster evaporation of the selected organic components and a higher initial packing density of the mixed particles. These results contributed to the mature and stable preparation of submicron silver pastes and provided a new approach for developing high-performance silver pastes with low-temperature pressure-less sintering properties. © 2024 Tianjin University. All rights reserved;
D O I：
10.11784/tdxbz202305036
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：974 / 981
相关论文
共 50 条
  • [21] Preparation of triethylamine stabilized silver nanoparticles for low-temperature sintering
    Wu, Jung-Tang
    Hsu, Steve Lien-Chung
    JOURNAL OF NANOPARTICLE RESEARCH, 2011, 13 (09) : 3877 - 3883
  • [22] Preparation of triethylamine stabilized silver nanoparticles for low-temperature sintering
    Jung-Tang Wu
    Steve Lien-Chung Hsu
    Journal of Nanoparticle Research, 2011, 13 : 3877 - 3883
  • [23] Pressureless sintering of submicron titanium carbide powders
    Fu, Zhezhen
    Koc, Rasit
    CERAMICS INTERNATIONAL, 2017, 43 (18) : 17233 - 17237
  • [24] Emerging Lead-free, High-temperature Die-attach Technology Enabled by Low-temperature Sintering of Nanoscale Silver Pastes
    Lu, Guo-Quan
    Zhao, Meihua
    Lei, Guangyin
    Calata, Jesus N.
    Chen, Xu
    Luo, Susan
    2009 INTERNATIONAL CONFERENCE ON ELECTRONIC PACKAGING TECHNOLOGY & HIGH DENSITY PACKAGING (ICEPT-HDP 2009), 2009, : 385 - +
  • [25] Low-temperature sintering of lanthanum strontium manganite-based contact pastes for SOFCs
    McCarthy, B. P.
    Pederson, L. R.
    Chou, Y. S.
    Zhou, X.-D.
    Surdoval, W. A.
    Wilson, L. C.
    JOURNAL OF POWER SOURCES, 2008, 180 (01) : 294 - 300
  • [26] Low-Temperature Sintering of Ag Composite Pastes with Different Metal Organic Decomposition Additions
    Xu, Zixuan
    Liu, Xun
    Li, Junjie
    Sun, Rong
    Liu, Li
    MATERIALS, 2023, 16 (06)
  • [27] Dense and nanostructured ceramics by low-temperature pressureless sintering of nanosized Y-TZP powders
    Duran, P.
    Villegas, M.
    Capel, F.
    Fernandez, J.F.
    Moure, C.
    Key Engineering Materials, 1997, 132-136 (Pt 2): : 739 - 742
  • [28] Surface modification of Cu flakes through Ag precipitation for low-temperature pressureless sintering bonding
    Park, S. W.
    Sugahara, T.
    Hatamura, M.
    Kagami, N.
    Sakamoto, S.
    Nagao, S.
    Suganuma, K.
    MATERIALS LETTERS, 2015, 151 : 68 - 71
  • [29] Pressureless Low Temperature Sintering of Ag Nanoparticles for Interconnects
    Wang, Shuai
    Ji, Hongjun
    Li, Mingyu
    Kim, Jongmyung
    Kim, Hongbae
    14TH INTERNATIONAL CONFERENCE ON ELECTRONIC MATERIALS AND PACKAGING (EMAP 2012), 2012,
  • [30] Pressureless Sintering and Properties of Silver Film for Electromagnetic Induction Heating
    电磁感应加热银膜的无压烧结及其性能研究
    Li, Meijuan (meijuanli@whut.edu.cn), 1694, Science Press (50): : 1694 - 1698
12345