High Transparency Nd: Y2O3 Ceramics Prepared with La2O3 and ZrO2 Additives

被引：0
|
作者：
Zhang, Lei [1 ]
Huang, Zuocai [1 ]
Pan, Wei [1 ]
机构：
[1] Zhang, Lei
[2] Huang, Zuocai
[3] Pan, Wei
来源：
Pan, Wei | 1600年 / Blackwell Publishing Inc., Postfach 10 11 61, 69451 Weinheim, Boschstrabe 12, 69469 Weinheim, Deutschland, 69469, Germany卷
关键词：
High transparency Nd: Y2O3 ceramics were prepared by vacuum sintering with La2O3 and ZrO2 sintering additives. The optimum in-line transmittance of the sintered Nd: Y2O3 is 80.98% at the wavelength of 1100 nm; for which the content of La2O3 and ZrO2 are 10.0 and 3.0 at.%; respectively. This specimen demonstrates homogeneous microstructure with the average grain size of 8.3 μm. The mechanism of sintering with La2O3 and ZrO2 aids and the optical properties was discussed. The absorption; emission cross section; and fluorescence lifetime have been estimated as 1.62 × 10-20 cm2; 5.13; ×; 10-20; cm2; and; 232; μs; respectively. Vickers hardness and the fracture toughness were measured of 9.18 GPa and 1.03 Mpa·m1/2; respectively. All the results indicate that Nd: Y2O3 transparent ceramic is a promising candidate for laser material. © 2014 The American Ceramic Society;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Article in Press
引用
收藏
相关论文
共 50 条
  • [41] Nanocrystalline Ceramics Based on the ZrO2–HfO2–Y2O3 System
    T. I. Panova
    V. B. Glushkova
    A. V. Lapshin
    V. P. Popov
    Glass Physics and Chemistry, 2003, 29 : 93 - 99
  • [42] Strain Localization during Diametral Compression of ZrO2(Y2O3) Ceramics
    I. N. Sevostyanova
    T. Yu. Sablina
    V. V. Gorbatenko
    S. N. Kulkov
    Technical Physics Letters, 2019, 45 : 943 - 946
  • [43] Atomic Force Microscopy of Deformation Relief in ZrO2 (Y2O3) Ceramics
    Sablina, T. Yu.
    Shlyakhova, G. V.
    Sevostyanova, I. N.
    Zuev, L. B.
    PROCEEDINGS OF THE INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS WITH HIERARCHICAL STRUCTURE FOR NEW TECHNOLOGIES AND RELIABLE STRUCTURES 2019, 2019, 2167
  • [44] Strain Localization during Diametral Compression of ZrO2(Y2O3) Ceramics
    Sevostyanova, I. N.
    Sablina, T. Yu.
    Gorbatenko, V. V.
    Kulkov, S. N.
    TECHNICAL PHYSICS LETTERS, 2019, 45 (09) : 943 - 946
  • [45] Mechanical properties of ZrO2 + 12% CeO2 ceramics with additives of CaO, Y2O3, Nb2O5
    Galakhov, A.V.
    Fomina, G.A.
    Il'icheva, A.A.
    Mikhajlina, N.A.
    Ogneupory i Tekhnicheskaya Keramika, 1994, (02): : 7 - 10
  • [46] Microstructure and High Temperature Friction and Wear Properties of Nanostructured ZrO2(Y2O3)-Al2O3 Ceramics
    Ouyang Jiahu
    Li Yufeng
    Wang Yujin
    Liang Xuesong
    Zhou Yu
    RARE METAL MATERIALS AND ENGINEERING, 2015, 44 : 799 - 803
  • [47] Effect of Y2O3 and La2O3 on the Sintering Behavior of Alumina
    Lee, Keun Bong
    Kang, Jong Bong
    KOREAN JOURNAL OF MATERIALS RESEARCH, 2016, 26 (02): : 90 - 94
  • [48] Porous ceramics based on the ZrO2(Y2O3)–Al2O3 system for filtration membranes
    L. V. Morozova
    M. V. Kalinina
    T. V. Khamova
    E. A. Vasil’eva
    O. A. Shilova
    Glass Physics and Chemistry, 2016, 42 : 408 - 413
  • [49] Porous ceramics based on the ZrO2(Y2O3)-Al2O3 system for filtration membranes
    Morozova, L. V.
    Kalinina, M. V.
    Khamova, T. V.
    Vasil'eva, E. A.
    Shilova, O. A.
    GLASS PHYSICS AND CHEMISTRY, 2016, 42 (04) : 408 - 413
  • [50] HIGH-TEMPERATURE CHARACTERIZATION OF SELFREINFORCED Si3N4 WITH ADDITIVES Y2O3 AND La2O3
    罗学涛
    Journal of Wuhan University of Technology-Materials Science, 1998, (01) : 1 - 6
12345