High Transparency Nd: Y2O3 Ceramics Prepared with La2O3 and ZrO2 Additives

被引：0
|
作者：
Zhang, Lei [1 ]
Huang, Zuocai [1 ]
Pan, Wei [1 ]
机构：
[1] Zhang, Lei
[2] Huang, Zuocai
[3] Pan, Wei
来源：
Pan, Wei | 1600年 / Blackwell Publishing Inc., Postfach 10 11 61, 69451 Weinheim, Boschstrabe 12, 69469 Weinheim, Deutschland, 69469, Germany卷
关键词：
High transparency Nd: Y2O3 ceramics were prepared by vacuum sintering with La2O3 and ZrO2 sintering additives. The optimum in-line transmittance of the sintered Nd: Y2O3 is 80.98% at the wavelength of 1100 nm; for which the content of La2O3 and ZrO2 are 10.0 and 3.0 at.%; respectively. This specimen demonstrates homogeneous microstructure with the average grain size of 8.3 μm. The mechanism of sintering with La2O3 and ZrO2 aids and the optical properties was discussed. The absorption; emission cross section; and fluorescence lifetime have been estimated as 1.62 × 10-20 cm2; 5.13; ×; 10-20; cm2; and; 232; μs; respectively. Vickers hardness and the fracture toughness were measured of 9.18 GPa and 1.03 Mpa·m1/2; respectively. All the results indicate that Nd: Y2O3 transparent ceramic is a promising candidate for laser material. © 2014 The American Ceramic Society;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Article in Press
引用
收藏
相关论文
共 50 条
  • [31] Dielectric spectroscopy of Al2O3 -Y2O3 -ZrO2 ternary composite ceramics
    Chen Dong-Ge
    Tang Xin-Gui
    Jia Zhen-Hua
    Wu Jun-Bo
    Xiong Hui-Fang
    ACTA PHYSICA SINICA, 2011, 60 (12)
  • [32] Microstructure and mechanical properties of ZrO2 fiber toughened Al2O3/ ZrO2(Y2O3) solidified ceramics prepared with high frequency induction zone melting
    Lan, Dehui
    Gao, Rui
    Liu, Xudong
    Zhu, Luyi
    Zheng, Yongting
    Liu, Juncheng
    JOURNAL OF ALLOYS AND COMPOUNDS, 2023, 967
  • [33] Influence of microwave heating on grain growth behavior and phase stability of nano Y2O3/La2O3 co-doped ZrO2 ceramics
    Zhang, Yanqiong
    Ren, Chunxiao
    Zhou, Ju
    Omran, Mamdouh
    Zhang, Fan
    Tang, Ju
    Chen, Guo
    CERAMICS INTERNATIONAL, 2024, 50 (06) : 8733 - 8741
  • [34] Highly transparent Nd-doped yttria ceramics fabricated by hot pressing with ZrO2 and La2O3 as sintering additives
    Gan, Lin
    Park, Young-Jo
    Zhu, Lin-Lin
    Kim, Ha-Neul
    Ko, Jae-Woong
    Lee, Jae-Wook
    JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 763 : 192 - 198
  • [35] SIC and Y2O3 co-coated zirconia composites prepared by Y2O3 coated ZrO2 powder
    Luo, J
    Stevens, R
    Dransfield, GP
    Birkby, I
    JOURNAL OF MATERIALS SCIENCE, 1997, 32 (13) : 3387 - 3392
  • [36] Mechanical Properties of Ceramics Prepared from a Nanocrystalline ZrO2 – 3 mol.% Y2O3 Powder
    G. Ya. Akimov
    V. M. Timchenko
    Refractories and Industrial Ceramics, 2004, 45 : 55 - 57
  • [37] SiC and Y2O3 co-coated zirconia composites prepared by Y2O3 coated ZrO2 powder
    J LUO
    R STEVENS
    G. P DRANSFIELD
    I BIRKBY
    Journal of Materials Science, 1997, 32 : 3387 - 3392
  • [38] Crystallization of ZrO2(Y2O3 3% mol) nanoscale powder prepared by precipitation
    刘惠文
    薛群基
    张平余
    王秀娥
    冯淑娱
    ChineseScienceBulletin, 1996, (12) : 988 - 994
  • [39] Effect of SiO2 on microstructure and transparency of Nd:Y2O3 ceramics
    Pathak, S. K.
    Singh, Gurvinderjit
    Gupta, S. M.
    Tiwari, V. S.
    Gupta, P. K.
    PROCEEDINGS OF THE 59TH DAE SOLID STATE PHYSICS SYMPOSIUM 2014 (SOLID STATE PHYSICS), 2015, 1665
  • [40] Fabrication and microstructure of hot pressed laminated Y2O3/Nd:Y2O3/Y2O3 transparent ceramics
    Gan, Lin
    Park, Young-Jo
    Kim, Haneul
    Kim, Jin-Myung
    Ko, Jae-Woong
    Lee, Jae-Wook
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2016, 36 (03) : 911 - 916
12345