High Transparency Nd: Y2O3 Ceramics Prepared with La2O3 and ZrO2 Additives

被引：0
|
作者：
Zhang, Lei [1 ]
Huang, Zuocai [1 ]
Pan, Wei [1 ]
机构：
[1] Zhang, Lei
[2] Huang, Zuocai
[3] Pan, Wei
来源：
Pan, Wei | 1600年 / Blackwell Publishing Inc., Postfach 10 11 61, 69451 Weinheim, Boschstrabe 12, 69469 Weinheim, Deutschland, 69469, Germany卷
关键词：
High transparency Nd: Y2O3 ceramics were prepared by vacuum sintering with La2O3 and ZrO2 sintering additives. The optimum in-line transmittance of the sintered Nd: Y2O3 is 80.98% at the wavelength of 1100 nm; for which the content of La2O3 and ZrO2 are 10.0 and 3.0 at.%; respectively. This specimen demonstrates homogeneous microstructure with the average grain size of 8.3 μm. The mechanism of sintering with La2O3 and ZrO2 aids and the optical properties was discussed. The absorption; emission cross section; and fluorescence lifetime have been estimated as 1.62 × 10-20 cm2; 5.13; ×; 10-20; cm2; and; 232; μs; respectively. Vickers hardness and the fracture toughness were measured of 9.18 GPa and 1.03 Mpa·m1/2; respectively. All the results indicate that Nd: Y2O3 transparent ceramic is a promising candidate for laser material. © 2014 The American Ceramic Society;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Article in Press
引用
收藏
相关论文
共 50 条
  • [21] Al2O3/ZrO2 (Y2O3) PREPARED BY COMBUSTION SYNTHESIS UNDER HIGH GRAVITY
    Zhang, Long
    Zhao, Zhongmin
    Song, Yigang
    Wang, Weiguo
    Liu, Hongbo
    INTERNATIONAL JOURNAL OF MODERN PHYSICS B, 2009, 23 (6-7): : 1148 - 1153
  • [22] A study on the effect of Y2O3, Gd2O3 and ZrO2 additives on the synthesis and properties of beryllium oxide ceramics
    Bogdanov, B. I.
    Markovska, I. G.
    JOURNAL OF THE BALKAN TRIBOLOGICAL ASSOCIATION, 2007, 13 (04): : 458 - 464
  • [23] ZrO2 and ZrO2/Y2O3 gate dielectrics prepared by evaporation and annealing processes
    Johansson, M
    Yousif, MYA
    Sareen, A
    Lundgren, P
    Bengtsson, S
    Södervall, U
    ASDAM '02, CONFERENCE PROCEEDINGS, 2002, : 279 - 282
  • [24] Fabrication of highly transparent Er3+, Yb3+:Y2O3 ceramics with La2O3/ZrO2 as sintering additives and the near-infrared and upconversion luminescence properties
    Wang, Nengli
    Zhang, Xiyan
    Bai, Zhaohui
    JOURNAL OF ALLOYS AND COMPOUNDS, 2020, 842
  • [25] RETENTION OF ADDITIVES IN Y2O3 GD2O3 LA2O3 AND ALPHA-AL2O3
    PASTOR, RC
    KIMURA, H
    PODOKSIK, L
    CERNICHIARI, O
    PEARSON, MA
    JOURNAL OF CHEMICAL PHYSICS, 1968, 48 (08): : 3830 - +
  • [26] Structural and optical properties of Tm:Y2O3 transparent ceramic with La2O3, ZrO2 as composite sintering aid
    Yi, Qing
    Zhou, Shengming
    Teng, Hao
    Lin, Hui
    Hou, Xiaorui
    Jia, Tingting
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2012, 32 (02) : 381 - 388
  • [27] DIFFUSION OF MN IN ZRO2(Y2O3)
    LAU, SK
    SINGHAL, SC
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1984, 131 (08) : C287 - C287
  • [28] Phase Transformations of Electrochemically Prepared Precursors of the TiO2–ZrO2–Y2O3 and TiO2–Al2O3–ZrO2–Y2O3 Oxide Systems
    A. F. Dresvyannikov
    E. V. Petrova
    L. I. Kashfrazyeva
    A. I. Khairullina
    Inorganic Materials, 2023, 59 : 742 - 748
  • [29] Effect of La2O3, Nd2O3 and Y2O3 on kinetics of high temperature phase transformation of kaolinite
    Kuang J.
    Hu J.
    Yuan W.
    1600, Cailiao Daobaoshe/ Materials Review (30): : 150 - 156and161
  • [30] Features of ZrO2–Y2O3 System Nanopowders with a Different Y2O3 Content
    S. E. Porozova
    I. V. Solnyshkov
    V. B. Kul’met’eva
    V. O. Shokov
    Refractories and Industrial Ceramics, 2015, 56 : 333 - 336
12345