Surface Morphology and Formation of Nanocrystals in an Amorphous Zr55Cu30Al10Ni5 Alloy under High-Pressure Torsion

被引:1
|
作者
Abrosimova, Galina [1 ]
Aksenov, Oleg [1 ]
Volkov, Nikita [1 ]
Matveev, Danila [1 ]
Pershina, Elena [1 ]
Aronin, Alexandr [1 ]
机构
[1] Osipyan Inst Solid State Phys RAS, Chernogolovka 142432, Russia
关键词
amorphous alloys; deformation; shear bands; crystallization; nanocrystals; SEVERE PLASTIC-DEFORMATION; BULK METALLIC-GLASS; SHEAR BANDS; MECHANICAL-PROPERTIES; DUCTILITY;
D O I
10.3390/met14070771
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A change in the structure of an amorphous Zr55Cu30Al10Ni5 alloy under deformation by high-pressure torsion (HPT) was studied by X-ray diffraction, high-resolution electron microscopy, scanning electron microscopy, and atomic force microscopy. It was found that the uneven distribution of deformation along the radius of the sample, characteristic of deformation by high-pressure torsion, led to the formation of an inhomogeneous structure. The formation of nanocrystals begins at the periphery of the sample. The threshold value of deformation required for crystallization onset was established; the formation of nanocrystals begins in areas with true deformation e = 4.83 or more. An increase in the deformation degree led to an increase in the height of steps on the deformed sample surface and an increase in the roughness of the surface. The thickness of an elementary step that was formed when one shear band came out to the surface was 10 nm, and its height was about 1 nm. It was found that large steps on the deformed surface of the sample had a complex structure and consisted of a large number of elementary steps. The results obtained are important for analyzing the stress distribution and the concentration of free volume in a deformed material, which affect the parameters of the amorphous-nanocrystalline structure formed.
引用
收藏
页数:14
相关论文
共 50 条
  • [41] Phase selection in the crystallization of Zr55Al10Ni5Cu30 amorphous alloy
    de Oliveira, MF
    Botta, WJ
    Kiminami, CS
    METASTABLE, MECHANICALLY ALLOYED AND NANOCRYSTALLINE MATERIALS, ISMANAM-2000, 2001, 360-3 : 107 - 112
  • [42] NMR investigations of the bulk metallic glass Zr55Cu30Al10Ni5
    Hoffmann, W
    Baenitz, M
    Lüders, K
    Gebert, A
    Eckert, J
    Schultz, L
    BULK METALLIC GLASSES, 1999, 554 : 95 - 100
  • [43] Cyclic softening of Zr55Al10Ni5Cu30 bulk amorphous alloy
    Zhang, QS
    Deng, YF
    Zhang, HF
    Ding, BZ
    Hu, ZQ
    JOURNAL OF MATERIALS SCIENCE LETTERS, 2003, 22 (23) : 1731 - 1734
  • [44] Compressive fracture of Zr55Al10Ni5Cu30 bulk amorphous alloy at high temperatures
    Zhang, QS
    Zhang, HF
    Ding, BZ
    Hu, ZQ
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 360 (1-2): : 280 - 284
  • [45] Compression fracture of bulk Zr55Al10Ni5Cu30 amorphous alloy at high temperature
    Zhang, QS
    Zhang, HF
    Wang, AM
    Ding, BZ
    Hu, ZQ
    ACTA METALLURGICA SINICA, 2002, 38 (08) : 835 - 838
  • [46] Compression fracture of bulk Zr55Al10Ni5Cu30 amorphous alloy at high temperature
    Zhang, Qingsheng
    Zhang, Haifeng
    Wang, Aimin
    Ding, Bingzhe
    Hu, Zhuangqi
    Jinshu Xuebao/Acta Metallurgica Sinica, 2002, 38 (08):
  • [47] Enhancement of ductility and plasticity of Zr55Cu30Al10Ni5 bulk glassy alloy by cold rolling
    Yokoyama, Y
    Yamano, K
    Fukaura, K
    Sunada, H
    Inoue, A
    MATERIALS TRANSACTIONS, 2001, 42 (04) : 623 - 632
  • [48] Reactive wetting of polycrystalline TiC by molten Zr55Cu30Al10Ni5 metallic glass alloy
    Shen, Ping
    Lin, Qiaoli
    Jiang, Qichuan
    Fujii, Hidetoshi
    Nogi, Kiyoshi
    JOURNAL OF MATERIALS RESEARCH, 2009, 24 (07) : 2420 - 2427
  • [49] The effect of impurities in zirconium on the formation and mechanical properties of Zr55Cu30Al10Ni5 metallic glass
    Liu, Ye
    Yin, Ziliang
    Lou, Hongbo
    Liang, Tao
    Dong, Hongliang
    Xu, Dazhe
    Song, Chao
    Wang, Qifan
    Chen, Songyi
    Zhang, Xin
    Chen, Xiehang
    Zeng, Zhidan
    Zeng, Qiaoshi
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2022, 596
  • [50] Influence of powder size on the crystallization behavior during laser solid forming Zr55Cu30Al10Ni5 bulk amorphous alloy
    Zhang, Yuanyuan
    Lin, Xin
    Wei, Lei
    Liu, Fenggang
    Huang, Weidong
    INTERMETALLICS, 2016, 76 : 1 - 9