Surface Morphology and Formation of Nanocrystals in an Amorphous Zr55Cu30Al10Ni5 Alloy under High-Pressure Torsion

被引:1
|
作者
Abrosimova, Galina [1 ]
Aksenov, Oleg [1 ]
Volkov, Nikita [1 ]
Matveev, Danila [1 ]
Pershina, Elena [1 ]
Aronin, Alexandr [1 ]
机构
[1] Osipyan Inst Solid State Phys RAS, Chernogolovka 142432, Russia
关键词
amorphous alloys; deformation; shear bands; crystallization; nanocrystals; SEVERE PLASTIC-DEFORMATION; BULK METALLIC-GLASS; SHEAR BANDS; MECHANICAL-PROPERTIES; DUCTILITY;
D O I
10.3390/met14070771
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A change in the structure of an amorphous Zr55Cu30Al10Ni5 alloy under deformation by high-pressure torsion (HPT) was studied by X-ray diffraction, high-resolution electron microscopy, scanning electron microscopy, and atomic force microscopy. It was found that the uneven distribution of deformation along the radius of the sample, characteristic of deformation by high-pressure torsion, led to the formation of an inhomogeneous structure. The formation of nanocrystals begins at the periphery of the sample. The threshold value of deformation required for crystallization onset was established; the formation of nanocrystals begins in areas with true deformation e = 4.83 or more. An increase in the deformation degree led to an increase in the height of steps on the deformed sample surface and an increase in the roughness of the surface. The thickness of an elementary step that was formed when one shear band came out to the surface was 10 nm, and its height was about 1 nm. It was found that large steps on the deformed surface of the sample had a complex structure and consisted of a large number of elementary steps. The results obtained are important for analyzing the stress distribution and the concentration of free volume in a deformed material, which affect the parameters of the amorphous-nanocrystalline structure formed.
引用
收藏
页数:14
相关论文
共 50 条
  • [21] Pressure effect on crystallization of Zr55CU30Al10Ni5 bulk metallic glass
    Liu, JJ
    Qiu, KQ
    Wang, AM
    Zhang, HF
    Ding, BZ
    Hu, ZQ
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2002, 18 (02) : 184 - 186
  • [22] Pressure effect on crystallization of Zr55Cu30Al10Ni5 bulk metallic glass
    Liu, Jianjun
    Qiu, Keqiang
    Wang, Aimin
    Zhang, Haifeng
    Ding, Bingzhe
    Hu, Zhuangqi
    Journal of Materials Science and Technology, 2002, 18 (02): : 184 - 186
  • [23] Effect of preparation method on the formation of amorphous alloy Zr55Al10Ni5Cu30
    Li, Qing-Feng
    Ren, Ying-Lei
    Yu, Bo
    Yuan, Xiao-Guang
    Qiu, Ke-Qiang
    Zhuzao/Foundry, 2007, 56 (10): : 1053 - 1056
  • [25] Oxidation behavior of Zr55Cu30Al10Ni5 BMG under static loading
    Wang, Xinyun
    Zhang, Mao
    Deng, Lei
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2017, 469 : 7 - 13
  • [26] Wettability of molten Zr55Cu30Al10Ni5 on alumina and zirconia
    Xu Qiangang
    Wu Baoling
    Zhang Haifeng
    Hu Zhuangqi
    RARE METALS, 2007, 26 (03) : 213 - 217
  • [27] Wetting behavior of Zr55Cu30Al10Ni5 melt on alumina
    Xu, QG
    Zhang, HF
    Hu, ZQ
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2005, 15 (01) : 45 - 50
  • [28] Wetting behavior of Zr55Cu30Al10Ni5 melt on alumina
    徐前刚
    张海峰
    胡壮麒
    Transactions of Nonferrous Metals Society of China, 2005, (01) : 45 - 50
  • [29] Influence of oxidation on the performance of Zr55Cu30Al10Ni5 BMG
    Zhang, Mao
    Yao, Di
    Cao, Zhiyong
    Li, Pan
    Zhou, Peng
    Wang, Xinyun
    INTERMETALLICS, 2016, 79 : 20 - 27
  • [30] Microstructure and mechanical properties of Zr55Cu30Al10Ni5 amorphous alloy with high-energy states produced by strip casting
    Zhang, C. Y.
    Yuan, G.
    Zhang, Y. X.
    Liu, C. Y.
    Wang, Y.
    Fang, F.
    Wang, G. D.
    Pang, Y. Y.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2021, 861 (861)