MODIFIED DOUBLE-CANTILEVER BEAM TEST FOR SULFIDE STRESS CRACKING OF TUBULAR STEELS

被引：2
|
作者：
ASTAFJEV, VI
SHMELEV, PS
TETJUEVA, TV
机构：
[1] NVNIIGG,RES INST,SARATOV 470071,RUSSIA
[2] VNIITNEFT,RES INST,SAMARA 443086,RUSSIA
来源：
CORROSION | 1994年 / 50卷 / 12期
关键词：
CRACK LENGTH; DOUBLE-CANTILEVER BEAM SPECIMEN; FLOW LOW-ALLOY STEELS; NACE STANDARD TM0177-90; STRESS; SULFIDE STRESS CRACKING; TUBULAR STEEL; WEDGE LOAD;
D O I：
10.5006/1.3293486
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A modification to the NACE International test procedure for determining the threshold stress intensity factor (K-ISSC) in assessing the sulfide stress cracking (SSC) resistance of low-alloy tubular steels was developed based on the use of Heady's second relationship for K-ISSC calculation. It was shown that only initial and equilibrium crack length, as well as initial wedge load, are needed to determine the K-ISSC value. Critical flaw sizes for steels investigated for use in inspection of tubulars were estimated from obtained K-ISSC values.
引用
收藏
页码：947 / 952
页数：6
相关论文
共 50 条
  • [31] Evaluation of debonding fracture toughness of paper-based friction materials by Double-Cantilever beam specimen
    Fujii, Tomoyuki
    Tohgo, Keiichiro
    Shimamura, Yoshinobu
    Wada, Takuya
    Ito, Yoichi
    Katayama, Nobuyuki
    Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 2012, 78 (790): : 902 - 911
  • [32] THE APPLICATION OF THE SLOW STRAIN RATE TEST METHOD FOR THE DEVELOPMENT OF LINEPIPE STEELS RESISTANT TO SULFIDE STRESS CRACKING
    MARGOTMARETTE, H
    BARDOU, G
    CHARBONNIER, JC
    CORROSION SCIENCE, 1987, 27 (10-11) : 1009 - +
  • [33] Pre-cracking behaviour in the single cantilever beam adhesion test
    S. Chauffaille
    J. Jumel
    M. E. R. Shanahan
    International Journal of Fracture, 2011, 169 : 133 - 144
  • [34] Pre-cracking behaviour in the single cantilever beam adhesion test
    Chauffaille, S.
    Jumel, J.
    Shanahan, M. E. R.
    INTERNATIONAL JOURNAL OF FRACTURE, 2011, 169 (02) : 133 - 144
  • [35] Effect of applied stress and microstructure on sulfide stress cracking resistance of pipeline steels subject to hydrogen sulfide
    Zhao, Ming-Chun
    Liu, Ming
    Atrens, Andrej
    Shan, Yi-Yin
    Yang, Ke
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 478 (1-2): : 43 - 47
  • [36] STRESS-ANALYSIS OF THE DOUBLE CANTILEVER BEAM SPECIMEN
    WHITNEY, JM
    COMPOSITES SCIENCE AND TECHNOLOGY, 1985, 23 (03) : 201 - 219
  • [37] Measuring the surface bonding energy: A comparison between the classical double-cantilever beam experiment and its nanoscale analog
    Pantzas, K.
    Fournel, F.
    Talneau, A.
    Patriarche, G.
    Le Bourhis, E.
    AIP ADVANCES, 2020, 10 (04)
  • [38] Role of microstructure on sulfide stress cracking of oil and gas pipeline steels
    Zhao, MC
    Tang, B
    Shan, YY
    Yang, K
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2003, 34A (05): : 1089 - 1096
  • [39] HIGH-STRENGTH STEELS WITH IMPROVED SULFIDE STRESS CRACKING RESISTANCE
    CHAVANE, A
    HABASHI, M
    PRESSOUYRE, GM
    GALLAND, J
    CORROSION, 1986, 42 (01) : 54 - 61
  • [40] THE ROLE OF NICKEL IN THE SULFIDE STRESS CRACKING OF LOW-ALLOY STEELS
    CRAIG, BD
    BROWNLEE, JK
    BRUNO, TV
    CORROSION, 1990, 46 (02) : 142 - 146
12345