MODIFIED DOUBLE-CANTILEVER BEAM TEST FOR SULFIDE STRESS CRACKING OF TUBULAR STEELS

被引：2
|
作者：
ASTAFJEV, VI
SHMELEV, PS
TETJUEVA, TV
机构：
[1] NVNIIGG,RES INST,SARATOV 470071,RUSSIA
[2] VNIITNEFT,RES INST,SAMARA 443086,RUSSIA
来源：
CORROSION | 1994年 / 50卷 / 12期
关键词：
CRACK LENGTH; DOUBLE-CANTILEVER BEAM SPECIMEN; FLOW LOW-ALLOY STEELS; NACE STANDARD TM0177-90; STRESS; SULFIDE STRESS CRACKING; TUBULAR STEEL; WEDGE LOAD;
D O I：
10.5006/1.3293486
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A modification to the NACE International test procedure for determining the threshold stress intensity factor (K-ISSC) in assessing the sulfide stress cracking (SSC) resistance of low-alloy tubular steels was developed based on the use of Heady's second relationship for K-ISSC calculation. It was shown that only initial and equilibrium crack length, as well as initial wedge load, are needed to determine the K-ISSC value. Critical flaw sizes for steels investigated for use in inspection of tubulars were estimated from obtained K-ISSC values.
引用
收藏
页码：947 / 952
页数：6
相关论文
共 50 条
  • [1] Numerical assessment of the Double-Cantilever Beam and Tapered Double-Cantilever Beam tests for the GIC determination of adhesive layers
    Teixeira, J. M. D.
    Campilho, R. D. S. G.
    da Silva, F. J. G.
    JOURNAL OF ADHESION, 2018, 94 (11): : 951 - 973
  • [2] Analytical corrections for double-cantilever beam tests
    Chen, T.
    Harvey, C. M.
    Wang, S.
    Silberschmidt, V. V.
    INTERNATIONAL JOURNAL OF FRACTURE, 2021, 229 (02) : 269 - 276
  • [3] Analytical corrections for double-cantilever beam tests
    T. Chen
    C. M. Harvey
    S. Wang
    V. V. Silberschmidt
    International Journal of Fracture, 2021, 229 : 269 - 276
  • [4] THE CALCULATION OF ADHESIVE FRACTURE ENERGIES FROM DOUBLE-CANTILEVER BEAM TEST SPECIMENS
    BLACKMAN, B
    DEAR, JP
    KINLOCH, AJ
    OSIYEMI, S
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1991, 10 (05) : 253 - 256
  • [5] Comparative evaluation of the Double-Cantilever Beam and Tapered Double-Cantilever Beam tests for estimation of the tensile fracture toughness of adhesive joints
    Lopes, R. M.
    Campilho, R. D. S. G.
    da Silva, F. J. G.
    Faneco, T. M. S.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2016, 67 : 103 - 111
  • [6] Self-similar crack propagation along a viscoelastic interface in a double-cantilever beam test
    Costa, J. P. Marquez
    Jumel, J.
    Badulescu, C.
    Stamoulis, G.
    MECHANICS OF TIME-DEPENDENT MATERIALS, 2024, 28 (02) : 337 - 362
  • [7] SULFIDE STRESS CRACKING OF NICKEL STEELS
    CRAIG, BD
    BROWNLEE, JK
    BRUNO, TV
    CORROSION, 1992, 48 (02) : 90 - 97
  • [8] MIXED-MODE FRACTURE OF BONDED JOINTS USING THE ASYMMETRIC TAPERED DOUBLE-CANTILEVER BEAM TEST
    Nunes, F. A. A.
    Campilho, R. D. S. G.
    IRF2018: PROCEEDINGS OF THE 6TH INTERNATIONAL CONFERENCE ON INTEGRITY-RELIABILITY-FAILURE, 2018, : 313 - 314
  • [9] Advanced beam model for fiber-bridging in unidirectional composite double-cantilever beam specimens
    Szekrényes, A
    Uj, J
    ENGINEERING FRACTURE MECHANICS, 2005, 72 (17) : 2686 - 2702
  • [10] DETERMINING PAINT ADHESION TO WOOD USING A UNIFORM DOUBLE-CANTILEVER BEAM TECHNIQUE
    KNAEBE, M
    WILLIAMS, RS
    JOURNAL OF TESTING AND EVALUATION, 1993, 21 (04) : 272 - 279
12345