BEHAVIOR OF SHORT FATIGUE CRACKS IN A MEDIUM CARBON-STEEL SUBJECTED TO BENDING

被引：5
|
作者：
WU, XJ
机构：
[1] Department of Mechanical and Process Engineering, University of Sheffield, Sheffield, S1 3JD, Mappin Street
来源：
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES | 1991年 / 14卷 / 2-3期
关键词：
D O I：
10.1111/j.1460-2695.1991.tb00665.x
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The fatigue process of a 0.45% carbon steel was studied with hour‐glass shaped specimens under rotatary bending. The plastic replication technique was applied to observe surface short fatigue cracks. Fatigue cracks initiated continuously with increasing number of cycles. The failure of a specimen largely depended on the number and distribution of these short cracks. The relationship of surface fatigue crack density to both stress amplitude and number of cycles was determined. Copyright © 1991, Wiley Blackwell. All rights reserved
引用
收藏
页码：369 / 372
页数：4
相关论文
共 50 条
  • [31] WEAR BEHAVIOR OF A CARBON-STEEL SUBJECTED TO AN ULTRASONIC VIBRATION EFFECT SUPERIMPOSED ON A STATIC CONTACT LOAD
    GOTO, H
    ASHIDA, M
    TERAUCHI, Y
    WEAR, 1986, 110 (02) : 169 - 181
  • [32] EXPERIMENTAL MODELING AND OPTIMIZATION OF TURNING MEDIUM CARBON-STEEL
    HASSAN, GA
    SULIMAN, SMA
    INTERNATIONAL JOURNAL OF PRODUCTION RESEARCH, 1990, 28 (06) : 1057 - 1065
  • [33] DISTRIBUTION OF CORROSION FATIGUE CRACK LENGTHS IN CARBON-STEEL .2. THE DISTRIBUTED CRACKS WHICH INTERACT AND COALESCE
    ISHIHARA, S
    SHIOZAWA, K
    MIYAO, K
    BULLETIN OF THE JSME-JAPAN SOCIETY OF MECHANICAL ENGINEERS, 1985, 28 (236): : 194 - 201
  • [34] MEDIUM CARBON-STEEL ALLOY DESIGN FOR WEAR APPLICATIONS
    SALESKY, WJ
    THOMAS, G
    WEAR, 1982, 75 (01) : 21 - 40
  • [35] THE BEHAVIOR AND IMPEDANCE OF THE PASSIVE STATE OF CARBON-STEEL
    GUO, XP
    IMAIZUMI, H
    KATOH, K
    DENKI KAGAKU, 1995, 63 (04): : 290 - 295
  • [36] INFLUENCE OF ALLOYING ON CYCLIC STRENGTH OF MEDIUM CARBON-STEEL
    VINOGRADOV, VE
    KHUDENKO, MA
    STEEL IN THE USSR, 1986, 16 (10): : 498 - 500
  • [37] SURFACE MELTING OF A MEDIUM CARBON-STEEL BY LASER TREATMENT
    CARBUCICCHIO, M
    MEAZZA, G
    PALOMBARINI, G
    SAMBOGNA, G
    JOURNAL OF MATERIALS SCIENCE, 1983, 18 (05) : 1543 - 1548
  • [38] EFFECT OF COMPOUNDING ON THE ADHESION OF RUBBER TO MEDIUM CARBON-STEEL
    REEVES, LA
    PACKHAM, DE
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 1992, 25 (1A) : A14 - A19
  • [39] STUDY ON THE EFFECT OF UNDERSTRESS ON FATIGUE LIFE OF SMOOTH SPECIMEN OF CARBON-STEEL UNDER ROTATING BENDING AND REVERSED TORSION - (ON BEHAVIOR OF CRACK-PROPAGATION)
    TOKAJI, K
    ANDO, Z
    YAMADA, T
    BULLETIN OF THE JSME-JAPAN SOCIETY OF MECHANICAL ENGINEERS, 1981, 24 (188): : 273 - 281
  • [40] The behavior of short fatigue cracks during Very High Cycle (VHCF) Fatigue of duplex stainless steel
    Krupp, U.
    Giertler, A.
    Soeker, M.
    Fu, H.
    Doenges, B.
    Christ, H. -J.
    Huesecken, A.
    Pietsch, U.
    Fritzen, C. -P.
    Ludwig, W.
    ENGINEERING FRACTURE MECHANICS, 2015, 145 : 197 - 209
12345