Failure Behavior of an Aluminide Coating on a Co-Base Superalloy during High-Temperature Oxidation in Air

被引：0
|
作者：
P. S. Liu
K. M. Liang
S. R. Gu
机构：
[1] Tsinghua University,Department of Materials Science and Engineering
[2] Chinese Academy of Sciences,Institute of Metal Research
来源：
Oxidation of Metals | 2000年 / 54卷
关键词：
aluminide coating; Co-base superalloy; high-temperature oxidation; corrosion nodule;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A surface-morphology change has been observed for an aluminide coating on the Co-base superalloy DZ40M during oxidation at 1100°C in air. The oxide formed on the coating remained an even grayish-white color during the stable oxidation stage, whereas, dark-colored corrosion nodules were observed when oxidation of the coating accelerated. The number of nodules increased with time, along with growth of the nodules, eventually covering the entire surface which signified failure.
引用
收藏
页码：277 / 283
页数：6
相关论文
共 50 条
  • [41] High-temperature mechanical properties in laser welds of Co-base superalloy and its improvement by laser surface melting
    Makino, Y
    Kimura, S
    Honda, K
    INTERNATIONAL CONFERENCE ON INTEGRITY OF HIGH-TEMPERATURE WELDS, 1998, : 193 - 199
  • [42] Phase transformation of Al-Ti coatings on Co-base superalloy DZ40M during high temperature oxidation
    Liu, PS
    Sun, XF
    Jin, T
    Guan, HR
    Hu, ZQ
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 1998, 8 (04) : 582 - 587
  • [43] High-temperature oxidation lifetime prediction for aluminide coatings in air
    Liu, Peisheng
    Liang, Kaiming
    Gu, Shouren
    Qinghua Daxue Xuebao/Journal of Tsinghua University, 2003, 43 (06): : 766 - 768
  • [44] PHASE TRANSFORMATION OF Al-Ti COATINGS ON Co-BASE SUPERALLOY DZ40M DURING HIGH TEMPERATURE OXIDATION
    Liu Peisheng
    TransactionsofNonferrousMetalsSocietyofChina, 1998, (04) : 51 - 56
  • [45] EFFECT OF ALUMINIDE COATING ON HIGH-CYCLE FATIGUE BEHAVIOR OF A NICKEL-BASE HIGH-TEMPERATURE ALLOY
    PASKIET, GF
    BOONE, DH
    SULLIVAN, CP
    JOURNAL OF THE INSTITUTE OF METALS, 1972, 100 (NFEB): : 58 - &
  • [46] Oxidation Behavior of Pd-modified aluminide coating at high temperature
    Li, MJ
    Sun, XF
    Guan, HR
    Jiang, XX
    Hu, ZQ
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2003, 19 (03) : 213 - 217
  • [47] Oxidation Behavior of Pd-Modified Aluminide Coating at High Temperature
    Mengjin LI
    Journal of Materials Science & Technology, 2003, (03) : 213 - 217
  • [48] HIGH-TEMPERATURE NITRIDATION OF FE-BASE, NI-BASE AND CO-BASE ALLOYS
    BARNES, JJ
    LAI, GY
    JOURNAL OF METALS, 1988, 40 (11): : 104 - 104
  • [49] HIGH-TEMPERATURE OXIDATION OF ALUMINIDE COATINGS
    ELMAJID, Z
    LAMBERTIN, M
    MATERIALS SCIENCE AND ENGINEERING, 1987, 87 (1-2): : 205 - 210
  • [50] ROLE OF Y DURING HIGH-TEMPERATURE OXIDATION OF AN M-CR-AL-Y COATING ON AN NI-BASE SUPERALLOY
    TAWANCY, HM
    ABBAS, NM
    BENNETT, A
    SURFACE & COATINGS TECHNOLOGY, 1994, 68 : 10 - 16
12345