Failure Behavior of an Aluminide Coating on a Co-Base Superalloy during High-Temperature Oxidation in Air

被引：0
|
作者：
P. S. Liu
K. M. Liang
S. R. Gu
机构：
[1] Tsinghua University,Department of Materials Science and Engineering
[2] Chinese Academy of Sciences,Institute of Metal Research
来源：
Oxidation of Metals | 2000年 / 54卷
关键词：
aluminide coating; Co-base superalloy; high-temperature oxidation; corrosion nodule;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A surface-morphology change has been observed for an aluminide coating on the Co-base superalloy DZ40M during oxidation at 1100°C in air. The oxide formed on the coating remained an even grayish-white color during the stable oxidation stage, whereas, dark-colored corrosion nodules were observed when oxidation of the coating accelerated. The number of nodules increased with time, along with growth of the nodules, eventually covering the entire surface which signified failure.
引用
收藏
页码：277 / 283
页数：6
相关论文
共 50 条
  • [21] Main degradation way of aluminide coating on Co-base superalloys oxidized in air at high temperatures
    Liu, P.S.
    Liang, K.M.
    Gu, S.R.
    Sun, X.F.
    Guan, H.R.
    Jin, T.
    Yang, K.N.
    Cailiao Gongcheng/Journal of Materials Engineering, 2001, (03):
  • [22] Transport mechanisms during the high-temperature oxidation of ternary γ/γ′ Co-base model alloys
    Martin Weiser
    Richard J. Chater
    Barbara A. Shollock
    Sannakaisa Virtanen
    npj Materials Degradation, 3
  • [23] Transport mechanisms during the high-temperature oxidation of ternary γ/γ′ Co-base model alloys
    Weiser, Martin
    Chater, Richard J.
    Shollock, Barbara A.
    Virtanen, Sannakaisa
    NPJ MATERIALS DEGRADATION, 2019, 3 (01)
  • [24] EFFECT OF HEAT-TREATMENT ON PRECIPITATION BEHAVIOR AND HIGH-TEMPERATURE STRENGTH IN A WROUGHT CO-BASE SUPERALLOY
    IIZUKA, H
    TANAKA, M
    JOURNAL OF MATERIALS SCIENCE, 1986, 21 (08) : 2803 - 2811
  • [25] HIGH-TEMPERATURE OXIDATION BEHAVIORS OF NI-BASE AND CO-BASE SUPERALLOYS
    BI, XF
    GOTO, KS
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1987, 51 (11) : 1060 - 1068
  • [26] Carbide Behavior during High Temperature Creep in DZ40M Co-base Superalloy
    Wenhui JIANG
    Xiangdong YAO
    Hengrong GUAN and Zhuangqi HU(Institute of Metal Research
    Journal of Materials Science & Technology, 1999, (06) : 515 - 518
  • [27] Carbide behavior during high temperature creep in DZ40M Co-base superalloy
    Jiang, Wenhui
    Yao, Xiangdong
    Guan, Hengrong
    Hu, Zhuangqi
    Journal of Materials Science and Technology, 1999, 15 (06): : 515 - 518
  • [28] Carbide behavior during high temperature creep in DZ40M co-base superalloy
    Jiang, WH
    Yao, XD
    Guan, HR
    Hu, ZQ
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 1999, 15 (06) : 515 - 518
  • [29] High temperature oxidation behavior for aluminide coating on the single crystal superalloy containing rhenium
    Liu, Chun-Ting
    Sun, Xiao-Feng
    Guan, Heng-Rong
    Hangkong Cailiao Xuebao/Journal of Aeronautical Materials, 2003, 23 (SUPPL.): : 118 - 122
  • [30] Abnormal oxidation behavior of β-NiAl base aluminide coating on a nickel-base superalloy
    Xiaofeng, Sun
    Hengrong, Guan
    Tao, Jin
    Taofeng, An
    Zhuangqi, Hu
    International Journal of Materials and Product Technology, 2001, (SPEC ISS. VOL.2) : 734 - 739
12345