Reliability of adhesion strength of the Sn-9Zn-1.5Ag-0.5Bi/Cu during isothermal aging

The reliability of adhesion strength of the Sn-9Zn-1.5Ag-0.5Bi/Cu during isothermal aging has been investigated. Due to the growth and decomposition of the intermetallic compound (IMC), the adhesion strength varies with aging at 150°C from 100, 400, and 700–1,000 h as wetted at 250°C for 60 sec. The IMC layers are determined at the Sn-9Zn-1.5Ag-0.5Bi/Cu interface by an x-ray diffractometer (XRD), an optical microscope (OM), a scanning electron microscope (SEM), an energy-dispersive spectroscope (EDS), and a transmission electron microscope (TEM). The adhesion strength has been investigated by the pull-off test. The results show that the Cu6Sn5, Cu5Zn8, and Ag3Sn IMCs are identified at the Sn-9Zn-1.5Ag-0.5Bi/Cu interface as aging. The adhesion strengths are 12.44±0.58, 8.57±0.43, 5.50±0.78, 4.32±0.78, and 3.32±0.43 MPa for aging times of 0 h, 100 h, 400 h, 700 h, and 1,000 h, respectively.