Brazing of zirconia with AgCuTi and SnAgTi active filler metals

被引：0
|
作者：
T. H. Chuang
M. S. Yeh
Y. H. Chai
机构：
[1] National Taiwan University,the Institute of Materials Science and Engineering
[2] Chung-Hua University,the Department of Mechanical Engineering
[3] NEC Electronics,the Micro Design and Development Division
[4] Inc.,undefined
来源：
Metallurgical and Materials Transactions A | 2000年 / 31卷
关键词：
Contact Angle; Material Transaction; Exothermic Peak; Interfacial Reaction; Filler Metal;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The self-brazing of partially stabilized zirconia using Ag27Cu3Ti and Sn10Ag4Ti active filler metals is investigated. It was shown that the contact angles of Ag27Cu3Ti and Sn10Ag4Ti on zirconia decreased with the increase of brazing temperature and remained constant at about 34 deg and 44 deg above 900 °C, respectively. The flexural strengths were 227 and 137 MPa for ZrO2/Ag27Cu3Ti/ZrO2 and ZrO2/Sn10Ag4Ti/ZrO2, respectively, after brazing at 900 °C for 10 minutes.
引用
收藏
页码：1591 / 1597
页数：6
相关论文
共 50 条
  • [41] DEVELOPMENT OF FILLER METALS AND PROCEDURES FOR VACUUM BRAZING OF ALUMINUM
    WERNER, WJ
    SLAUGHTE.GM
    GURTNER, FB
    WELDING JOURNAL, 1972, 51 (02) : S64 - &
  • [42] VACUUM BRAZING OF TITANIUM WITH ALUMINUM FILLER METALS.
    Takemoto, Tadashi
    Nakamura, Hideyuki
    Okamoto, Ikuo
    Keikinzoku/Journal of Japan Institute of Light Metals, 1986, 36 (10): : 627 - 632
  • [43] How oxygen affects nickel brazing filler metals
    Peaslee, Robert L.
    Walter, Peter F.
    Welding Journal (Miami, Fla), 1995, 74 (01): : 61 - 66
  • [44] Effect of Ag on the properties of solders and brazing filler metals
    Wang, He
    Xue, Song-bai
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2016, 27 (01) : 1 - 13
  • [45] LAMINATED BRAZING FILLER METALS FOR TITANIUM ASSEMBLIES.
    LAN, S.W.
    1982, V 61 (N 10): : 23 - 28
  • [46] Research Progress of Filler Metals for Brazing Diamond Tools
    Long W.
    Hao Q.
    Fu Y.
    Huang G.
    Wu M.
    Wang Y.
    1600, Cailiao Daobaoshe/ Materials Review (34): : 23138 - 23144
  • [47] Effect of Ag on the properties of solders and brazing filler metals
    He Wang
    Song-bai Xue
    Journal of Materials Science: Materials in Electronics, 2016, 27 : 1 - 13
  • [48] DEVELOPMENT OF BRAZING FILLER METALS FOR HIGH TEMPERATURE SERVICE
    GILLILAND, RG
    SLAUGHTE.GM
    WELDING JOURNAL, 1969, 48 (10) : S463 - +
  • [49] Microstructure and interfacial reactions of vacuum brazing titanium alloy to stainless steel using an AgCuTi filler metal
    Yue, X.
    He, P.
    Feng, J. C.
    Zhang, J. H.
    Zhu, F. Q.
    MATERIALS CHARACTERIZATION, 2008, 59 (12) : 1721 - 1727
  • [50] HOW OXYGEN AFFECTS NICKEL BRAZING FILLER METALS
    PEASLEE, RL
    WALTER, PF
    WELDING JOURNAL, 1995, 74 (01) : 61 - 66
12345