Brazing of zirconia with AgCuTi and SnAgTi active filler metals

被引：0
|
作者：
T. H. Chuang
M. S. Yeh
Y. H. Chai
机构：
[1] National Taiwan University,the Institute of Materials Science and Engineering
[2] Chung-Hua University,the Department of Mechanical Engineering
[3] NEC Electronics,the Micro Design and Development Division
[4] Inc.,undefined
来源：
Metallurgical and Materials Transactions A | 2000年 / 31卷
关键词：
Contact Angle; Material Transaction; Exothermic Peak; Interfacial Reaction; Filler Metal;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The self-brazing of partially stabilized zirconia using Ag27Cu3Ti and Sn10Ag4Ti active filler metals is investigated. It was shown that the contact angles of Ag27Cu3Ti and Sn10Ag4Ti on zirconia decreased with the increase of brazing temperature and remained constant at about 34 deg and 44 deg above 900 °C, respectively. The flexural strengths were 227 and 137 MPa for ZrO2/Ag27Cu3Ti/ZrO2 and ZrO2/Sn10Ag4Ti/ZrO2, respectively, after brazing at 900 °C for 10 minutes.
引用
收藏
页码：1591 / 1597
页数：6
相关论文
共 50 条
  • [21] Brazing of silicon nitride with reactive filler metals
    Trehan, V
    Trickey, S
    Indacochea, JE
    Lugscheider, E
    Buschke, I
    Tillmann, W
    SCIENCE AND ENGINEERING OF COMPOSITE MATERIALS, 1999, 8 (02): : 107 - 112
  • [22] Thermodynamics characteristics of AgCuZnSn brazing filler metals
    Wang X.-X.
    Du Q.-B.
    Peng J.
    Cui D.-T.
    Yu T.-Y.
    Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2018, 28 (06): : 1159 - 1167
  • [23] WETTABILITY OF BRAZING FILLER METALS ON MOLYBDENUM AND TZM
    MCDONALD, MM
    KELLER, DL
    HEIPLE, CR
    HOFMANN, WE
    WELDING JOURNAL, 1989, 68 (10) : S389 - S395
  • [24] Physical properties of selected brazing filler metals
    Arenas, MF
    Acoff, VL
    Reddy, RG
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2004, 9 (05) : 423 - 429
  • [25] Liquation of Brazing Filler Metals - Good or Bad?
    Kay, Dan
    WELDING JOURNAL, 2010, 89 (09) : 36 - 39
  • [26] Wettability of brazing filler metals on molybdenum and TZM
    McDonald, M.M.
    Keller, D.L.
    Heiple, C.R.
    Hofmann, W.E.
    Welding Journal (Miami, Fla), 1989, 68 (10):
  • [27] HOW TO CHOOSE BRAZING FILLER METALS.
    Weymueller, Carl R.
    Welding Design and Fabrication, 1984, 57 (07): : 33 - 39
  • [28] FLOW OF ALUMINUM DIP BRAZING FILLER METALS
    WOODS, RA
    ROBINSON, IB
    WELDING JOURNAL, 1974, 53 (10) : S440 - S445
  • [29] Filler metals, brazing processing and reliability for diamond tools brazing: A review
    Zhang, Liang
    JOURNAL OF MANUFACTURING PROCESSES, 2021, 66 : 651 - 668
  • [30] Application of amorphous and microcrystalline filler metals for brazing of beryllium with metals
    Kalin, BA
    Fedotov, VT
    Sevryukov, ON
    Grigoryev, AE
    Plyuschev, AN
    Ivanov, VM
    Strebkov, YS
    JOURNAL OF NUCLEAR MATERIALS, 1996, 233 : 945 - 948
12345