Brazing of zirconia with AgCuTi and SnAgTi active filler metals

被引：0
|
作者：
T. H. Chuang
M. S. Yeh
Y. H. Chai
机构：
[1] National Taiwan University,the Institute of Materials Science and Engineering
[2] Chung-Hua University,the Department of Mechanical Engineering
[3] NEC Electronics,the Micro Design and Development Division
[4] Inc.,undefined
来源：
Metallurgical and Materials Transactions A | 2000年 / 31卷
关键词：
Contact Angle; Material Transaction; Exothermic Peak; Interfacial Reaction; Filler Metal;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The self-brazing of partially stabilized zirconia using Ag27Cu3Ti and Sn10Ag4Ti active filler metals is investigated. It was shown that the contact angles of Ag27Cu3Ti and Sn10Ag4Ti on zirconia decreased with the increase of brazing temperature and remained constant at about 34 deg and 44 deg above 900 °C, respectively. The flexural strengths were 227 and 137 MPa for ZrO2/Ag27Cu3Ti/ZrO2 and ZrO2/Sn10Ag4Ti/ZrO2, respectively, after brazing at 900 °C for 10 minutes.
引用
收藏
页码：1591 / 1597
页数：6
相关论文
共 50 条
  • [1] Brazing of zirconia with AgCuTi and SnAgTi active filler metals
    Chuang, TH
    Yeh, MS
    Chai, YH
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2000, 31 (06): : 1591 - 1597
  • [2] Active Brazing of C/C Composite to Copper by AgCuTi Filler Metal
    Zhang, Kexiang
    Xia, Lihong
    Zhang, Fuqin
    He, Lianlong
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2016, 47A (05): : 2162 - 2176
  • [3] Active Brazing of C/C Composite to Copper by AgCuTi Filler Metal
    Kexiang Zhang
    Lihong Xia
    Fuqin Zhang
    Lianlong He
    Metallurgical and Materials Transactions A, 2016, 47 : 2162 - 2176
  • [4] Development of Active Nickel Based Brazing Filler Metals
    Sandin, Thomas A.
    BRAZING AND SOLDERING, PROCEEDINGS, 2006, : 367 - 372
  • [5] Brazing filler metals
    Way, Matthew
    Willingham, Jack
    Goodall, Russell
    INTERNATIONAL MATERIALS REVIEWS, 2020, 65 (05) : 257 - 285
  • [6] Vacuum brazing of MgAl2O4 transparent ceramics with AgCuTi active filler metal
    Zhu, Chengjun
    Shang, Changpei
    Hanjie Xuebao/Transactions of the China Welding Institution, 2015, 36 (04): : 101 - 105
  • [7] WELDING AND BRAZING FILLER METALS
    SLAUGHTE.GM
    CANONICO, DA
    NUCLEAR ENGINEERING AND DESIGN, 1971, 17 (02) : 181 - &
  • [8] WETTABILITY OF BRAZING FILLER METALS
    KELLER, DL
    MCDONALD, MM
    HEIPLE, CR
    JOHNS, WL
    HOFMANN, WE
    WELDING JOURNAL, 1990, 69 (10) : 31 - 34
  • [9] Graphene nanoplatelets reinforced AgCuTi composite filler for brazing SiC ceramic
    Song, Yanyu
    Liu, Duo
    Hu, Shengpeng
    Song, Xiaoguo
    Cao, Jian
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2019, 39 (04) : 696 - 704
  • [10] Brazing Filler Metals for Joining Refractory Metals
    不详
    WELDING JOURNAL, 2011, 90 (09) : 64 - 64
12345