Preparation and degradation characteristics of poly (d, l-lactide) composite films

被引：0
|
作者：
Lei Chen
Yuhua Yan
Jianhua Li
Shipu Li
机构：
[1] Wuhan University of Technology,Biomedical Materials and Engineering Research Center
来源：
Journal of Wuhan University of Technology-Mater. Sci. Ed. | 2007年 / 22卷
关键词：
poly (d, l-lactic acid) (PDLLA); chitosan (CHI); -TCP; nerve growth factor (NGF); degradation characteristics;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
PDLLA/CHI/β-TCP/NGF composite films were prepared by a solvent evaporation method. The degradation characteristics of the poly (d, l-lactide) composite films were studied in vitro and in vivo. The acidity produced by poly (d, l-lactide) materials was not obvious. Adding chitosan and β-TCP can relieve the acidity problem and improve strength performance of films. The NGF has influences on the degradation characteristics of films. It is verified that PDLLA/CHI/β-TCP/NGF composite films prepared by solvent evaporation method have excellent degradation characteristics. It can be used as a perfect biomaterial for repairing nerve injuries.
引用
收藏
相关论文
共 50 条
  • [41] Preparation of porous composites consisting of apatite and poly(D,L-lactide)
    Nagata, F
    Miyajima, T
    Yokogawa, Y
    BIOCERAMICS 15, 2003, 240-2 : 167 - 170
  • [42] Degradation of Poly(L-lactide) Films under Ultraviolet Irradiation and Water Bath
    Zhang, Chunmei
    Man, Changzhen
    Wang, Weiwei
    Jiang, Long
    Dan, Yi
    POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING, 2011, 50 (08) : 810 - 817
  • [43] Degradation of Poly(L-Lactide) films under ultravioletInduced photografting and sterilization conditions
    Janorkar, Amol V.
    Metters, Andrew T.
    Hirt, Douglas E.
    JOURNAL OF APPLIED POLYMER SCIENCE, 2007, 106 (02) : 1042 - 1047
  • [44] Enzymatic degradation of Poly(D,L-lactide) and its, blends with poly(vinyl acetate)
    Mahalik, J. P.
    Madras, Giridhar
    JOURNAL OF APPLIED POLYMER SCIENCE, 2006, 101 (01) : 675 - 680
  • [45] The Preparation and Property Research on Laponite-Poly (L-lactide) Composite Film
    Zhou, Guo-xian
    Yuan, Ming-wei
    Jiang, Lin
    Yuan, Ming-long
    Li, Hong-li
    ADVANCED ENGINEERING MATERIALS III, PTS 1-3, 2013, 750-752 : 1919 - 1923
  • [46] Enzymatic degradation of poly(D,L-lactide) and its blends with poly(vinyl acetate)
    Mahalik, J.P.
    Madras, Giridhar
    Journal of Applied Polymer Science, 2006, 101 (01): : 675 - 680
  • [47] Preparation and characterization of a novel electrospun spider silk fibroin/poly(D,L-lactide) composite fiber
    Zhou, Shaobing
    Peng, Hongsen
    Yu, Xiongjun
    Zheng, Xiaotong
    Cui, Wenguo
    Zhang, Zairong
    Li, Xiaohong
    Wang, Jianxin
    Weng, Jie
    Jia, Wenxiang
    Li, Fei
    JOURNAL OF PHYSICAL CHEMISTRY B, 2008, 112 (36): : 11209 - 11216
  • [48] Poly(ε-caprolactone-co-D,L-lactide)/silk fibroin composite materials:: Preparation and characterization
    Kesenci, K
    Motta, A
    Fambri, L
    Migliaresi, C
    JOURNAL OF BIOMATERIALS SCIENCE-POLYMER EDITION, 2001, 12 (03) : 337 - 351
  • [49] Accelerated hydrolytic degradation of Poly(L-lactide)/Poly(D-lactide) stereocomplex up to late stage
    Tsuji, Hideto
    Tsuruno, Tomonori
    POLYMER DEGRADATION AND STABILITY, 2010, 95 (04) : 477 - 484
  • [50] Relationship between crystallization state and degradation behavior of poly(l-lactide)/four-armed poly(d,l-lactide)-block-poly(d-lactide) blends with different poly(d-lactide) block lengths
    Dai, Suyang
    Jiang, Ni
    Ning, Zhenbo
    Gan, Zhihua
    POLYMER INTERNATIONAL, 2021, 70 (05) : 667 - 678
12345