High-Temperature Oxidation Behavior of Sputtered IN 738 Nanocrystalline Coating

被引：9
|
作者：
Shujiang Geng
Fuhui Wang
Shenglong Zhu
机构：
[1] The Chinese Academy of Sciences,State Key Laboratory for Corrosion and Protection, Institute of Metal Research
来源：
Oxidation of Metals | 2002年 / 57卷
关键词：
Sputtering; IN 738 alloy; nanocrystalline coating; oxidation;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A sputtered nanocrystalline coating of IN 738 alloy was obtained by means of magnetron sputtering. The isothermal oxidation behavior at 800, 900, and 1000°C and the cyclic oxidation behavior at 950°C of the coating were studied in comparison with IN 738 cast alloy. The results indicated that a double external oxide scale was formed on the nanocrystalline coating at 900, 950, and 1000°C without internal oxide and nitride. The scale consisted in an outer mixture of Cr2O3, TiO2, and NiCr2O4 and an inner, continuous Al2O3 layer, which offered good adhesive and protectiveness. However, at 800°C a continuous Al2O3 scale could not be formed during oxidation of nanocrystalline coating and aluminum was still oxidized internally.
引用
收藏
页码：231 / 243
页数：12
相关论文
共 50 条
  • [31] Influence of Re on High-Temperature Oxidation Behavior of MCrAIY Type Coating Alloys
    Shahzad Salem
    Zhang Yuduo
    Wang Haifeng
    Yang Zhigang
    Zhang Chi
    RARE METAL MATERIALS AND ENGINEERING, 2015, 44 : 316 - 319
  • [32] High-temperature oxidation of an aluminized NiCr alloy formed by a magnetron-sputtered Al diffusion coating
    Brossard, JM
    Balmain, J
    Sanchette, F
    Bonnet, G
    OXIDATION OF METALS, 2005, 64 (1-2): : 43 - 61
  • [33] High-Temperature Oxidation of an Aluminized NiCr Alloy formed by a Magnetron-Sputtered Al Diffusion Coating
    J. -M. Brossard
    J. Balmain
    F. Sanchette
    G. Bonnet
    Oxidation of Metals, 2005, 64 : 43 - 61
  • [34] The oxidation behavior of high-temperature aluminides
    I. C. I. Okafor
    R. G. Reddy
    JOM, 1999, 51 : 35 - 40
  • [35] Oxidation Behavior of a Sputtered Ni–5Cr–5Al Nanocrystalline Coating
    Guofeng Chen
    Hanyi Lou
    Oxidation of Metals, 2000, 53 : 467 - 479
  • [36] Deposition of Iridium Coating on Pure Tungsten and High-Temperature Oxidation Behavior at 1300 K
    Zhang, Jifu
    Chen, Dongchu
    Zhang, Xueying
    Niu, Ben
    Wang, Biao
    Li, Runxia
    COATINGS, 2022, 12 (11)
  • [37] High-temperature oxidatiOn behavior of laser-aided additively manufactured NiCrAlY coating
    Ansari, M.
    Shoja-Razavi, R.
    Barekat, M.
    Man, H. C.
    CORROSION SCIENCE, 2017, 118 : 168 - 177
  • [38] Structure and high temperature oxidation properties of magnetron sputtered CrSiN coating
    Xu, Xiang-Min
    Zhang, Hao
    Shang, Jin
    Luo, Chen-Gang
    Duo, Shu-Wang
    Rengong Jingti Xuebao/Journal of Synthetic Crystals, 2015, 44 : 155 - 158
  • [39] Comparison of thermal expansion and oxidation behavior of various high-temperature coating materials and superalloys
    Haynes, JA
    Pint, BA
    Porter, WD
    Wright, IG
    MATERIALS AT HIGH TEMPERATURES, 2004, 21 (02) : 87 - 94
  • [40] Study on the High-temperature Coating in Preventing Oxidation and Decarburization
    Lin, Shengyao
    Tang, Luwen
    Zeng, Jianmin
    MATERIALS PROCESSING TECHNOLOGIES, PTS 1 AND 2, 2011, 154-155 : 1830 - 1833
12345