High-Temperature Oxidation Behavior of Sputtered IN 738 Nanocrystalline Coating

被引：9
|
作者：
Shujiang Geng
Fuhui Wang
Shenglong Zhu
机构：
[1] The Chinese Academy of Sciences,State Key Laboratory for Corrosion and Protection, Institute of Metal Research
来源：
Oxidation of Metals | 2002年 / 57卷
关键词：
Sputtering; IN 738 alloy; nanocrystalline coating; oxidation;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A sputtered nanocrystalline coating of IN 738 alloy was obtained by means of magnetron sputtering. The isothermal oxidation behavior at 800, 900, and 1000°C and the cyclic oxidation behavior at 950°C of the coating were studied in comparison with IN 738 cast alloy. The results indicated that a double external oxide scale was formed on the nanocrystalline coating at 900, 950, and 1000°C without internal oxide and nitride. The scale consisted in an outer mixture of Cr2O3, TiO2, and NiCr2O4 and an inner, continuous Al2O3 layer, which offered good adhesive and protectiveness. However, at 800°C a continuous Al2O3 scale could not be formed during oxidation of nanocrystalline coating and aluminum was still oxidized internally.
引用
收藏
页码：231 / 243
页数：12
相关论文
共 50 条
  • [11] Cyclic Oxidation Behavior of Sputtered Nanocrystalline Coating with Yttrium Additions in Air
    Yu, Ping
    Wang, Wen
    Wang, Fuhui
    Zhu, Shenglong
    HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 7, PTS 1 AND 2, 2008, 595-598 : 1163 - 1171
  • [12] HIGH-TEMPERATURE DRY SLIDING WEAR BEHAVIOR OF COLD-SPRAYED INCONEL 738 COATING
    Padmini, B. V.
    Bhosale, Digivijay G.
    Niranjan, H. B.
    Mathapati, Mahantayya
    Sampathkumaran, P.
    SURFACE REVIEW AND LETTERS, 2023, 30 (02)
  • [13] High-temperature oxidation behavior of PbTe and oxidation-resistive glass coating
    Chen, LD
    Goto, T
    Tu, R
    Hirai, T
    PROCEEDINGS ICT'97 - XVI INTERNATIONAL CONFERENCE ON THERMOELECTRICS, 1997, : 251 - 254
  • [14] Oxidation behavior of sputtered Ni-Cr-Al-Ti nanocrystalline coating
    Chen, G
    Lou, H
    SURFACE & COATINGS TECHNOLOGY, 2000, 123 (01): : 92 - 96
  • [15] High-temperature oxidation behavior and surface roughness evolution of VPSNiCrAlY coating
    Seo, D.
    Ogawa, K.
    Shoji, T.
    Murata, S.
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2008, 17 (01) : 136 - 143
  • [16] High temperature oxidation behavior of Inc-738/NiCrAlY/LaMA thermal barrier coating system
    Khorramirad, M. M.
    Rahimipour, M. R.
    Hadavi, S. M. M.
    Shirvani, K.
    SURFACE & COATINGS TECHNOLOGY, 2019, 364 : 70 - 80
  • [17] High-temperature oxidation and hot corrosion behavior of the Inconel 738LC coating with and without Al2O3-CNTs
    Alsultani, Kadhim F.
    Majidi, Hassan Sh.
    Abdulameer, Sara
    Karkush, Mahdi
    JOURNAL OF THE MECHANICAL BEHAVIOR OF MATERIALS, 2023, 32 (01)
  • [18] Effect of Shot Peening of Substrate Surface on Cyclic Oxidation Behavior of Sputtered Nanocrystalline Coating
    Huang Ding
    Qiao Yanxin
    Yang Lanlan
    Wang Jinlong
    Chen Minghui
    Zhu Shenglong
    Wang Fuhui
    ACTA METALLURGICA SINICA, 2023, 59 (05) : 668 - 678
  • [19] Oxidation behavior of a sputtered Ni-5Cr-5Al nanocrystalline coating
    Chen, GF
    Lou, HY
    OXIDATION OF METALS, 2000, 53 (5-6): : 467 - 479
  • [20] Oxidation and hot corrosion behavior of sputtered nanocrystalline coating of superalloy K52
    Wang, F.
    Tian, X.
    Li, Q.
    Li, L.
    Peng, X.
    THIN SOLID FILMS, 2008, 516 (16) : 5740 - 5747
12345