Improved oxidation resistance properties of Si3N4/O′-SiAlON composite ceramics by a repeated sintering method

被引：2

作者：

Ma, Haiqiang ^{[1
]}

Bao, Chonggao ^{[1
]}

机构：

[1] Xi An Jiao Tong Univ, State Key Lab Mech Behav Mat, Xian 710049, Shaanxi, Peoples R China

来源：

INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY | 2022年 / 19卷 / 05期

基金：

中国国家自然科学基金;

关键词：

oxidation resistance; Si3N4/O '-SiAlON composites; two-time sintering; weight gain; SILICON-NITRIDE; MECHANICAL-PROPERTIES; FLEXURAL STRENGTH; LIQUID-PHASE; MICROSTRUCTURE; BEHAVIOR;

D O I：

10.1111/ijac.14102

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Si3N4/O'-SiAlON composite ceramics with superior oxidation resistance properties were fabricated by a repeated sintering method. The effects of sintering time on the phase evolution, microstructure, and oxidation resistance properties of the Si3N4/O'-SiAlON composite ceramics were investigated. The results indicated that the content of the O'-SiAlON phase and the densification of Si3N4/O'-SiAlON composite ceramics increased after two-time sintering. Furthermore, the thickness of the oxide layer of the Si3N4/O'-SiAlON composite ceramics after oxidation at 1100-1500 degrees C for 30 h was not significant. Compared to the oxidation weight gain after the one-time sintering process, the oxidation weight gain of Si3N4/O'-SiAlON composite ceramics was 0.432 mg/cm(2) after two-time sintering when oxidized at 1500 C for 30 h, which was reduced by 43.3%. The mechanism of the improved oxidation resistance properties was ascribed to the formation of more O'-SiAlON and the enhancement of the densification.

引用

页码：2905 / 2915

页数：11

共 50 条

[21] Oxidation resistance of Si3N4 ceramics with aluminum ion implantation
Feng, Jianji
Li, Guoqing
Zhang, Changrui
Mu, Zongxin
Qi, Min
Liu, Hongze
Zhou, Xingui
Kuei Suan Jen Hsueh Pao/ Journal of the Chinese Ceramic Society, 2004, 32 (09): : 1060 - 1063
[22] Significantly enhanced thermal shock resistance of α-Si3N4/O′-Sialon composite coating toughened by two-dimensional h-BN nanosheets on porous Si3N4 ceramics
Liu, Huichao
Wang, Binglei
He, Yuxuan
Wang, Chao
Song, Guihong
Wu, Yusheng
Wang, Zhanjie
CERAMICS INTERNATIONAL, 2022, 48 (20) : 30510 - 30516
[23] Effect of aluminum on the sintering of β-Si3N4 ceramics
Zhang Ling
Li Fushen
Xue Wendong
Sun Jialin
Lu Xionggang
RARE METAL MATERIALS AND ENGINEERING, 2007, 36 : 334 - 336
[24] Sintering reactions of mixtures of Y-α'-SiAlON and α-Si3N4
Ukyo, Y.
Suda, A.
Masaki, H.
Niihara, K.
Key Engineering Materials, 159-160 : 221 - 228
[25] Effect of starting Si3N4 powder type and sintering conditions on grain morphology of α-SiAlON ceramics
Kushan, SR
Mandal, H
BRITISH CERAMIC TRANSACTIONS, 2002, 101 (01): : 35 - 37
[26] EFFECTIVE SINTERING AIDS FOR SI3N4 CERAMICS
NEGITA, K
JOURNAL OF MATERIALS SCIENCE LETTERS, 1985, 4 (06) : 755 - 758
[27] Effect of starting Si3N4 powder type and sintering conditions on the grain morphology of α-SiAlON ceramics
Kushan, SR
Mandal, H
NITRIDES AND OXYNITRIDES 2, 2002, 383 : 31 - 36
[28] Sintering reactions of mixtures of Y-α′-SiAlON and α-Si3N4
Ukyo, Y
Suda, A
Masaki, H
Niihara, K
NOVEL SYNTHESIS AND PROCESSING OF CERAMICS, 1999, 159-1 : 221 - 227
[29] Microstructure and ambient properties of a Sialon composite prepared by hot pressing and reactive sintering of β-Si3N4 coated with Al2O3
Ghosh, G
Vaynman, S
Fine, ME
Hsu, SM
JOURNAL OF MATERIALS RESEARCH, 1999, 14 (03) : 881 - 890
[30] Microstructure and ambient properties of a Sialon composite prepared by hot pressing and reactive sintering of β–Si3N4 coated with Al2O3
G. Ghosh
S. Vaynman
M. E. Fine
S. M. Hsu
Journal of Materials Research, 1999, 14 : 881 - 890

← 1 2 3 4 5 →