Sintering optimisation and solution annealing of high nitrogen nickel free austenitic stainless steels prepared by PIM

被引：11
|
作者：
Cui, D. W. [1 ,2 ]
Qu, X. H. [2 ]
Guo, P. [1 ]
Li, K. [2 ]
机构：
[1] Weifang Univ, Dept Machinery, Weifang 261061, Peoples R China
[2] Univ Sci & Technol Beijing, Sch Mat Sci & Engn, Beijing 100083, Peoples R China
来源：
POWDER METALLURGY | 2010年 / 53卷 / 01期
基金：
中国国家自然科学基金;
关键词：
High nitrogen nickel free; Austenitic stainless steel; Sintering optimisation; Solution annealing; CORROSION;
D O I：
10.1179/174329008X284930
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The effects of various sintering parameters (temperature, time and nitrogen pressure) on the density, nitrogen content and the mechanical properties of high nitrogen nickel free austenitic stainless steel (0Cr-17Mn-11Mo-3N) prepared by powder injection moulding were investigated, and the influence of solution annealing on the microstructure and mechanical properties was also discussed. The results show that the optimal sintering conditions are as follows: sintering temperature 1300 degrees C, sintering time 2 h and nitrogen pressure 0.1 MPa, under which a favourable combination of the relative density of 99.1% and the nitrogen content of 0.78 wt-% can be obtained. After solution annealing at 1150 degrees C for 90 min, the yield strength and ultimate tensile strength can reach 580 and 885 MPa respectively, which are about 2.9 and 1.7 times greater than those of 316L Metal Injection Molding (MIM) stainless steel. Before solution annealing, the sintered specimens mainly consist of gamma-austenite, alpha-ferrite and network of Cr2N phase, while after solution annealing, they reveals a fully austenitic structure without any intergranular nitrides.
引用
收藏
页码：91 / 95
页数：5
相关论文
共 50 条
  • [41] Corrosion resistance of nickel-free austenitic stainless steels and their nanocomposites with hydroxyapatite in Ringer's solution
    Tulinski M.
    Jurczyk M.
    Materials Science Forum, 2011, 674 : 159 - 163
  • [42] Factors inducing intergranular fracture in nickel-free high nitrogen austenitic stainless steel produced by solution nitriding
    Tsuchiyama, Toshihiro
    Fujii, Yousuke
    Terazawa, Yusuke
    Nakashima, Koichi
    Ando, Tomohiro
    Takaki, Setsuo
    ISIJ INTERNATIONAL, 2008, 48 (06) : 861 - 867
  • [43] Impact properties of high-nitrogen austenitic stainless steels
    Yuan, Zhizhong
    Dai, Qixun
    Cheng, Xiaonong
    Chen, Kangmin
    Xu, Wenwei
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 475 (1-2): : 202 - 206
  • [44] Progress on welding of high nitrogen alloyed austenitic stainless steels
    Holmberg B.
    Welding in the World, 2002, 46 (1-2) : 3 - 9
  • [45] Mechanical Behaviour of Aged High Nitrogen Austenitic Stainless Steels
    N. C. Santhi Srinivas
    V. V. Kutumbarao
    Transactions of the Indian Institute of Metals, 2011, 64 : 331 - 337
  • [46] Mechanical Behaviour of Aged High Nitrogen Austenitic Stainless Steels
    Srinivas, N. C. Santhi
    Kutumbarao, V. V.
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2011, 64 (4-5) : 331 - 337
  • [47] Progress on welding of high nitrogen alloyed austenitic stainless steels
    Holmberg, B.
    Welding Research Abroad, 2004, 50 (11): : 1 - 7
  • [48] AUSTENITIC STAINLESS STEELS OF HIGH STRENGTH AFTER SOLUTION TREATMENTS
    KOHL, H
    STAHL UND EISEN, 1968, 88 (19): : 1063 - &
  • [49] Post-sintering thermal treatment of nitrogen containing pressed and sintered and PIM stainless steels
    Hwang, K. S.
    Hsueh, Y. W.
    POWDER METALLURGY, 2007, 50 (02) : 165 - 171
  • [50] Effects of nitrogen on microstructure of cold deformed high nitrogen austenitic stainless steels
    Wang, Wei
    Chen, Shu-Mei
    Yan, Wei
    Zhao, Li-Jun
    Shan, Yi-Yin
    Yang, Ke
    Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment, 2010, 31 (07): : 59 - 65
12345