The effect of porosity on the laser induced damage threshold of TiO2 and ZrO2 single layer films

Monolayer ZrO2 and TiO2 films were prepared on BK7 glass by physical vapor deposition (PVD) and were subsequently annealed for 1 h at 300 degrees C. By using the transmission spectra of two samples and the envelope method, the refractive index dispersion and extinction coefficients have been calculated. Laser induced damage threshold (LIDT) measurement shows that despite slight differences between the extinction coefficients of the two samples, the LIDT parameter of the ZrO2 film is greater than that of the TiO2 film. This fact leads us to consider thermal conductivity as an important parameter for interpreting the LIDT difference. According to our theoretical analysis, as a consequence of increase in the number of thermal barriers along poorer film, its thermal conductivity, and hence LIDT, decreased, which is in agreement with our experimental results. The measured porosity of the two samples shows higher porosity for TiO2 single layer, which is in agreement with atomic force (AFM) images. The gradual and smooth damage morphology of ZrO2 observed in optical images implies higher thermal conductivity than TiO2. (C) 2010 Elsevier Ltd. All rights reserved.