Effect of preaging on precipitation hardening in Al-Si-Mg alloys

被引：0
|
作者：
Tan, YH [1 ]
Lee, SL [1 ]
Wang, PS [1 ]
机构：
[1] Natl Cent Univ, Dept Mech Engn, Chungli 32054, Taiwan
来源：
THERMEC '97 - INTERNATIONAL CONFERENCE ON THERMOMECHANICAL PROCESSING OF STEELS AND OTHER MATERIALS, VOLS I-II | 1997年
关键词：
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The effect of various water quenching temperature and duration time of precipitation hardened Al-7Si-0.65Mg cast alloy is investigated by differential scanning calorimeter, electrical onductivity, hardness and tensile properties measurements. The results shows a positive response to 95 degrees C water quenched from solid solution treatment. The largest hardened rate can be obtained at 95 degrees C water-quenching for 60 minutes duration time in natural aging. The tensile strength and hardness following 95 degrees C quenched is found to be higher than that 25 degrees C and 60 degrees C water quenched in the shorter artificial aging time. High temperature water-quenching parameters available to high temperature(>180 degrees C) artificial aging treatment with the shorter aging time.
引用
收藏
页码：959 / 964
页数：6
相关论文
共 50 条
  • [41] EFFECT OF THE COMPOSITION AND MICROALLOYING WITH STRONTIUM ON THE STRUCTURE AND PROPERTIES OF AL-SI-MG ALLOYS
    GANIEV, IN
    VAKHOBOV, AV
    SEMENOVA, ON
    METAL SCIENCE AND HEAT TREATMENT, 1983, 25 (7-8) : 623 - 625
  • [42] The effect of interacting defects on the HCF behavior of Al-Si-Mg aluminum alloys
    Ben Ahmed, Amal
    Houria, Mohamed Iben
    Fathallah, Raouf
    Sidhom, Habib
    JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 779 : 618 - 629
  • [43] Effect of Prestraining and Preaging on Properties of Al-Mg-Si Alloys Before and After Plane Baking
    Ren, Xianwei
    Huang, Yuanchun
    Li, Ying
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (07) : 4496 - 4501
  • [44] The effect of Zn on precipitation in Al-Mg-Si alloys
    Saito, Takeshi
    Wenner, Sigurd
    Osmundsen, Elisa
    Marioara, Calin D.
    Andersen, Sigmund J.
    Royset, Jostein
    Lefebvre, Williams
    Holmestad, Randi
    PHILOSOPHICAL MAGAZINE, 2014, 94 (21) : 2410 - 2425
  • [45] The effect of Cu on precipitation in Al-Mg-Si alloys
    Marioara, C. D.
    Andersen, S. J.
    Stene, T. N.
    Hasting, H.
    Walmsley, J.
    Van Helvoort, A. T. J.
    Holmestad, R.
    PHILOSOPHICAL MAGAZINE, 2007, 87 (23) : 3385 - 3413
  • [46] Predicting primary dendrite arm spacing in Al-Si-Mg alloys: effect of Mg alloying
    Ridgeway, Colin D.
    Gu, Cheng
    Luo, Alan A.
    JOURNAL OF MATERIALS SCIENCE, 2019, 54 (13) : 9907 - 9920
  • [47] Effect of Si Content on Dynamic Recrystallization of Al-Si-Mg Alloys During Hot Extrusion
    Yuna Wu
    Hengcheng Liao
    Jian Yang
    Kexin Zhou
    JournalofMaterialsScience&Technology, 2014, 30 (12) : 1271 - 1277
  • [48] Analyzing Age Hardening Behaviors of an Al-Si-Mg Cast Alloy
    Zhou, Ying
    Wang, Guiqing
    MANUFACTURING PROCESS TECHNOLOGY, PTS 1-5, 2011, 189-193 : 3945 - +
  • [49] Effect of Intermetallics and Tramp Elements on Porosity Formation and Hardness of Al-Si-Mg and Al-Si-Cu-Mg Alloys
    Mohamed, A. M. A.
    Samuel, E.
    Samuel, A. M.
    Samuel, F. H.
    Songmene, V
    Doty, H. W.
    INTERNATIONAL JOURNAL OF METALCASTING, 2023, 17 (02) : 664 - 681
  • [50] HARDENING OF AL-MG-SI ALLOYS AND EFFECT OF PARTICLE STRUCTURE
    Gulbrandsen-Dahl, Sverre
    Marioara, C. D.
    Pedersen, Ketill Olav
    Marthinsen, Knut
    THERMEC 2011, PTS 1-4, 2012, 706-709 : 283 - +
12345