Effects of Nb content on the microstructure and magnetic properties of Fe-6.5wt.%Si alloy

被引：0
|
作者：
Cheng, Zhaoyang [1 ]
Liu, Jing [1 ]
Xiang, Zhidong [1 ]
Lin, Xifeng [1 ]
Zhu, Shang [1 ]
Chen, Wensi [1 ]
Zhu, Jiachen [1 ]
机构：
[1] Wuhan Univ Sci & Technol, State Key Lab Refractories & Met, Wuhan 430081, Peoples R China
来源：
OPTOELECTRONICS AND ADVANCED MATERIALS-RAPID COMMUNICATIONS | 2016年 / 10卷 / 1-2期
关键词：
Fe-6.5 wt.% Si alloy; Nb micro-alloyed; Microstructure; Magnetic properties; HIGH-SILICON STEEL; SI; EVOLUTION; TEXTURE; SHEET; WORKABILITY;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effects of adding different contents of Nb on microstructure and magnetic properties of Fe-6.5wt.%Si alloy were investigated. The results show that the addition of a suitable amount of Nb to Fe-6.5wt.%Si alloys has improved the ductility of the alloy by precipitating Nb-Fe-Si intermetallics. The precipitated Nb-Fe-Si particles have refined the grains and lowering the Si content in the matrix, the latter effect has resulted in the reduction of the ordered phases or the degree of long range order in the alloy. However, when the Nb content is 2.0wt.%, the numbers of precipitates are too high and starting to pin the movement of dislocations, which has an adverse effect on the processability of the alloy. Though the Fe-6.5Si-1.5Nb (wt.%) alloy showed better magnetic properties than the Fe-6.5Si-2.0Nb (wt.%) alloy, the addition of Nb would deteriorate the magnetic properties of Fe-6.5wt.%Si alloy. Thus, the addition of Nb should be less than 1.5 wt.% to balance the processability and magnetic properties of Fe-6.5wt.%Si alloy.
引用
收藏
页码：82 / 86
页数：5
相关论文
共 50 条
  • [21] Effects of warm rolling reduction on the microstructure, texture and magnetic properties of Fe-6.5 wt% Si steel
    Cai, Guojun
    Li, Changsheng
    Cai, Ban
    Wang, Qiwen
    JOURNAL OF MATERIALS RESEARCH, 2016, 31 (12) : 1773 - 1783
  • [22] Effects of deformation temperature on the microstructure, ordering and mechanical properties of Fe-6.5 wt% Si alloy with columnar grains
    Mo, Yuanke
    Zhang, Zhihao
    Fu, Huadong
    Pan, Hongjiang
    Xie, Jianxin
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 594 : 111 - 117
  • [23] Effects of boron on microstructure and mechanical properties of Fe-6.5 wt.%Si alloy fabricated by directional solidification
    Fu, Huadong
    Zhang, Zhihao
    Wu, Xuesong
    Xie, Jianxin
    INTERMETALLICS, 2013, 35 : 67 - 72
  • [24] Development of strong {001}⟨210⟩ texture and magnetic properties in Fe-6.5wt.%Si thin sheet produced by rolling method
    Liu, J. L.
    Sha, Y. H.
    Zhang, F.
    Yang, H. P.
    Zuo, L.
    JOURNAL OF APPLIED PHYSICS, 2011, 109 (07)
  • [25] Effect of Annealing Temperature on Soft Magnetic Properties of Cold Rolled 0.30 mm Thick Fe-6.5wt.%Si Foils
    Fang, X. S.
    Lin, J. P.
    Liang, Y. F.
    Ye, F.
    Zhang, L. Q.
    Chen, G. L.
    JOURNAL OF MAGNETICS, 2011, 16 (02) : 177 - 180
  • [26] Improvement of magnetic properties of an Fe-6.5 wt.% Si alloy by directional solidification
    Fu, Huadong
    Zhang, Zhihao
    Jiang, Yanbin
    Xie, Jianxin
    MATERIALS LETTERS, 2011, 65 (09) : 1416 - 1419
  • [27] Improvement of magnetic properties of an Fe-6.5 wt. % Si alloy by directional recrystallization
    Zhang, Z. W.
    Chen, G.
    Bei, H.
    Ye, F.
    Chen, G. L.
    Liu, C. T.
    APPLIED PHYSICS LETTERS, 2008, 93 (19)
  • [28] Fe-6.5wt.%Si High Silicon Steel Sheets Produced by Cold Rolling
    Ye, Feng
    Liang, Y. F.
    Wang, Y. L.
    Lin, J. P.
    Chen, G. L.
    THERMEC 2009, PTS 1-4, 2010, 638-642 : 1428 - 1433
  • [29] Study on Compressibility According to Mixing Ratio and Milling Time of Fe-6.5wt.%Si
    Kim, Jaemin
    Lee, Seonbong
    MATERIALS, 2024, 17 (08)
  • [30] Microstructure, mechanical and magnetic properties of melt extracted Fe-6.5 wt.%Si microwires
    Wang, Shuai
    Liang, Yongfeng
    Ye, Feng
    Geng, Guihong
    Lin, Junpin
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2017, 249 : 325 - 330
12345