Mechanism of Ce promoting SO2 resistance of MnO x /γ-Al2O3: An experimental and DFT study

被引：10

作者：

Zhang, Xiaopeng ^{[1
]}

Li, Zhuofeng ^{[1
]}

Zhao, Jijun ^{[2
]}

Cui, Yuezong ^{[1
]}

Tan, Bojian ^{[1
]}

Wang, Jinxin ^{[1
]}

Zhang, Chengxiang ^{[1
]}

He, Gaohong ^{[1
]}

机构：

[1] Dalian Univ Technol, Sch Petr & Chem Engn, State Key Lab Fine Chem, Panjin 124221, Liaoning, Peoples R China

[2] Dalian Univ Technol, Key Lab Mat Modificat Laser Ion & Electron Beams, Minist Educ, Dalian 116024, Peoples R China

来源：

KOREAN JOURNAL OF CHEMICAL ENGINEERING | 2017年 / 34卷 / 07期

基金：

中国国家自然科学基金;

关键词：

Selective Catalytic Reduction; MnOx; Density Functional Theory; Modification; SO2; Poisoning; SELECTIVE CATALYTIC-REDUCTION; LOW-TEMPERATURE SCR; MNOX-CEO2; CATALYST; OXIDE CATALYSTS; NO REDUCTION; NH3; PERFORMANCE; OXIDATION; AMMONIA; ZR;

D O I：

10.1007/s11814-017-0092-3

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

Various physico-chemical techniques and theoretical chemistry computations are used to obtain a deep insight into the mechanism of Ce improving SO2 resistance of the catalyst Mn0.4Ce (x) /Al2O3 (x stands for the molar ratio of Ce : Al). Theoretical computation with density functional theory (DFT) shows that Ce modification enhances the adsorption energy of SO2 adsorbed on Ce surrounding, resulting in the preferential adsorption of SO2 on Ce surrounding. It protects the surface Mn from SO2 poisoning, leading to a better SO2 resistance. FT-IR and TG results are in good accordance with DFT results. FT-IR results suggest that absorption peaks related to SO4 (2-) cannot be detected in Mn0.4Ce0.12/Al2O3. Moreover, TG results show that weight loss peaks due to sulfated MnO (x) decomposition disappears after Ce addition. Therefore, Ce modification inhibits sulfates formation on active components lead to a better resistance to SO2 of Mn0.4Ce0.12/Al2O3.

引用

页码：2065 / 2071

页数：7

共 50 条

[41] 助剂MnO2对Na2CO3-γ-Al2O3吸附SO2和NO性能的影响
杜冰
宗保宁
罗一斌
王维家
石油化工, 2012, 41 (12) : 1418 - 1423
[42] γ-Al2O3表面吸附SO2、NOx的机理分析
郭大为
石油学报(石油加工), 2010, 26 (02) : 235 - 241
[43] CO OXIDATION OVER CUCR/AL2O3 CATALYSTS IN PRESENCE OF SO2
MULINA, TV
FILIPOV, AV
CHUMACHENKO, VA
REACTION KINETICS AND CATALYSIS LETTERS, 1988, 37 (01): : 95 - 100
[44] A deep insight into arsenic adsorption over γ-Al2O3 in the presence of SO2/NO
Huang, Yongda
Yang, Yuhan
Hu, Hongyun
Xu, Mian
Liu, Huan
Li, Xian
Wang, Xinye
Yao, Hong
PROCEEDINGS OF THE COMBUSTION INSTITUTE, 2019, 37 (03) : 2951 - 2957
[45] Effects of SO2 on NO reduction with methanol over Ag/Al2O3 catalyst
Zhu, Tianle
Hao, Jiming
Fu, Lixin
Cui, Xiangyu
Wang, Yanji
Huanjing Kexue/Environmental Science, 2002, 23 (04):
[46] CuO/γ-Al2O3脱除烟气中SO2的研究
谢国勇
刘振宇
刘有智
郭向云
燃料化学学报, 2003, (05) : 385 - 389
[47] Experimental determination of the activation energies of CH4, SO2 and O2 reactions on Cr2O3/γ - Al2O3
Hernandez Guiance, S. N.
Coria, I. D.
Irurzun, I. M.
Mola, E. E.
CHEMICAL PHYSICS LETTERS, 2016, 660 : 123 - 126
[48] Effect of iron doping on SO2 and H2O resistance of honeycomb cordierite-based Mn–Ce/Al2O3 catalyst for NO removal at low temperature
Cheng-zhi Wang
Yong-gang Zhao
Cheng Zhang
Xin Yan
Peng Cao
Research on Chemical Intermediates, 2018, 44 : 3135 - 3150
[49] Effect of relative humidity on O3 and NO2 oxidation of SO2 on α-Al2O3 particles
Liu, Wenjun
He, Xiang
Pang, Shufeng
Zhang, Yunhong
ATMOSPHERIC ENVIRONMENT, 2017, 167 : 245 - 253
[50] Adsorption of NO and O2 on MnO2 and (MnO2)3/Al2O3
Li, Hui
Wang, Denghui
Hui, Shien
Applied Surface Science, 2021, 569

← 1 2 3 4 5 →