Study on the process characteristics of vacuum hot pressing sintering of TiNiNb alloy based on "near net shape forming"

被引：5
|
作者：
Liu Junwei [1 ]
Li Yong [1 ]
Lu Shiqiang [1 ]
Wan Jun [1 ]
Gao Wenliang [1 ]
机构：
[1] Nanchang Hangkong Univ, Key Lab M Crostruct Control Metall Mat Jiangxi Pr, Nanchang 330063, Jiangxi, Peoples R China
来源：
MATERIALS LETTERS | 2021年 / 294卷
关键词：
TiNiNb alloy; Vacuum hot pressing sintering; Relative density; Microstructure; MECHANICAL-PROPERTIES; MICROSTRUCTURE; NB; TI;
D O I：
10.1016/j.matlet.2021.129758
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The TiNiNb pre-alloyed powder prepared after mechanical alloying was used as experimental material, and TiNiNb alloy was prepared by vacuum hot pressing sintering method (temperature 900 degrees C, pressure 35 MPa, vacuum degree 1.6 x 10(-3) Pa). The relative density and microstructure evoultion were analyzed by a serial of testing methods, such as: XRD and SEM etc. The results showed that the TiNiNb pre-alloyed powder presented amorphous state, the relative density of TiNiNb alloy after vacuum hot pressing sintering was 98.8%, and the alloy was completely crystallized. The microstructure of vacuum hot-pressed TiNiNb alloy is uniform, mainly composed of Ti-Ni matrix phase, beta-Nb phase, (Ti,Nb)(2)Ni hard phase and a small amount of TiC impurity phase. (C) 2021 Elsevier B.V. All rights reserved.
引用
收藏
页数：3
相关论文
共 50 条
  • [11] Near-net-shape forming of 316L stainless steel powder under hot isostatic pressing
    Jeon, YC
    Kim, KT
    INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 1999, 41 (07) : 815 - 830
  • [12] Near-net-shape forming of 316L stainless steel powder under hot isostatic pressing
    Department of Mechanical Engineering, Pohang Univ. of Sci. and Technology, San 31 Hyoja-dong, Nam-ku, Pohang 790-784, Korea, Republic of
    不详
    Int J Mech Sci, 7 (815-830):
  • [13] Near net shape fabrication via vacuum plasma spray forming
    Balani, K
    Agarwal, A
    McKechnie, T
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2006, 59 (02): : 237 - 244
  • [14] Simulation of hot isostatic pressing of metal powder components to near net shape
    Svoboda, A
    Haggblad, HA
    Nasstrom, M
    ENGINEERING COMPUTATIONS, 1996, 13 (05) : 13 - &
  • [15] Simulation of hot isostatic pressing of metal powder components to near net shape
    Svoboda, Ales
    Häggblad, Hans-Åke
    Näsström, Mats
    Engineering Computations (Swansea, Wales), 1996, 13 (05): : 13 - 37
  • [16] Development of process parameters for manufacturing of near-net shape parts of rhenium using hot isostatic pressing
    Bryskin, BD
    Samarov, VN
    Kratt, EP
    RHENIUM AND RHENIUM ALLOYS, 1996, : 425 - 436
  • [17] 3D modelling of net-shape forming by hot isostatic pressing
    Dellis, C
    Abondance, D
    Baccino, R
    Moret, F
    HOT ISOSTATIC PRESSING, CONFERENCE PROCEEDINGS, 1996, : 139 - 143
  • [18] A new near net-shape forming process for alumina
    Sato, T
    Besshi, T
    Matsui, M
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1998, 79 (1-3) : 125 - 132
  • [19] Near net shape magnesium alloy components by superplastic forming and thixoforming
    Park, KP
    Birt, MJ
    Mawella, KJA
    ADVANCED PERFORMANCE MATERIALS, 1996, 3 (3-4): : 365 - 375
  • [20] Near net shape magnesium alloy components by superplastic forming and thixoforming
    Structural Materials Cent, Kent, United Kingdom
    Adv Perform Mater, 3-4 (365-375):
12345