Study on the process characteristics of vacuum hot pressing sintering of TiNiNb alloy based on "near net shape forming"

被引：5
|
作者：
Liu Junwei [1 ]
Li Yong [1 ]
Lu Shiqiang [1 ]
Wan Jun [1 ]
Gao Wenliang [1 ]
机构：
[1] Nanchang Hangkong Univ, Key Lab M Crostruct Control Metall Mat Jiangxi Pr, Nanchang 330063, Jiangxi, Peoples R China
来源：
MATERIALS LETTERS | 2021年 / 294卷
关键词：
TiNiNb alloy; Vacuum hot pressing sintering; Relative density; Microstructure; MECHANICAL-PROPERTIES; MICROSTRUCTURE; NB; TI;
D O I：
10.1016/j.matlet.2021.129758
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The TiNiNb pre-alloyed powder prepared after mechanical alloying was used as experimental material, and TiNiNb alloy was prepared by vacuum hot pressing sintering method (temperature 900 degrees C, pressure 35 MPa, vacuum degree 1.6 x 10(-3) Pa). The relative density and microstructure evoultion were analyzed by a serial of testing methods, such as: XRD and SEM etc. The results showed that the TiNiNb pre-alloyed powder presented amorphous state, the relative density of TiNiNb alloy after vacuum hot pressing sintering was 98.8%, and the alloy was completely crystallized. The microstructure of vacuum hot-pressed TiNiNb alloy is uniform, mainly composed of Ti-Ni matrix phase, beta-Nb phase, (Ti,Nb)(2)Ni hard phase and a small amount of TiC impurity phase. (C) 2021 Elsevier B.V. All rights reserved.
引用
收藏
页数：3
相关论文
共 50 条
  • [1] Near-net-shape forming of alumina powder under hot pressing and hot isostatic pressing
    Kim, KT
    Kwon, YS
    Kim, HG
    INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 1997, 39 (09) : 1011 - 1022
  • [2] Experimental Study on Near-Net-Shape Forming of Titanium Alloy Powders Complex Parts by Hot Isostatic Pressing
    Wang, Jiwei
    Wei, Qingsong
    Xue, Pengjv
    He, Yukun
    Shi, Yusheng
    TI-2011: PROCEEDINGS OF THE 12TH WORLD CONFERENCE ON TITANIUM, VOL III, 2012, : 1804 - +
  • [3] Near net shape forming process of a titanium alloy impeller
    Shi, K.
    Sham, D. B.
    Xu, W. C.
    Lu, Y.
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2007, 187 : 582 - 585
  • [4] Near-Net-Shape Tungsten-Rhenium Alloy Parts Produced by Plasma Spray Forming and Hot Isostatic Pressing
    Wang, Yueming
    Xiong, Xiang
    Zhao, Weizhong
    Xie, Lu
    Yan, Jianhui
    Min, Xiaobing
    Zheng, Feng
    MATERIALS TRANSACTIONS, 2014, 55 (04) : 713 - 721
  • [5] Hot isostatic pressing of near net shape components - process fundamentals and future challenges
    Broeckmann, Christoph
    POWDER METALLURGY, 2012, 55 (03) : 176 - 179
  • [6] Near-net-shape forming of ceramic powder under cold combination pressing and pressureless sintering
    Kim, HG
    Lee, HM
    Kim, KT
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 2001, 123 (02): : 221 - 228
  • [7] Direct Hot-pressing Makes Sintering of Near-net-shape Parts Quick and Easy
    Schreyer, Pascal
    CFI-CERAMIC FORUM INTERNATIONAL, 2009, 86 (04): : E39 - E40
  • [8] VACUUM HOT-PRESSING OF NEAR-NET-SHAPE STRUCTURAL PARTS WITH REP AND HYDRIDE POWDERS
    KAO, WH
    BLUNCK, RD
    BAJORAITIS, R
    KOSMAL, B
    JOURNAL OF METALS, 1981, 33 (09): : A28 - A28
  • [9] Hot pressing sintering process of tungsten alloy for polishing diamond
    Lin, Jia-Zhi
    Jin, Zhu-Ji
    Shi, Shuang-Ji
    Zhong, Xiu-Hong
    Jiang, Guan-Nan
    Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2015, 25 (03): : 682 - 689
  • [10] Dense and uniform Mo10W alloy prepared by combining a vacuum sintering process with a hot-pressing process
    Ding, Pengzhan
    Song, Hao
    Wang, Chengduo
    Wu, Xiaochao
    Li, Qingkui
    Cao, Wenbo
    MATERIALS SCIENCE AND TECHNOLOGY, 2024,
12345