Crack formation mechanisms in Al2O3/Kovar brazed joint

被引：6
|
作者：
Yu, Z. S. [1 ]
Yang, P. [1 ]
Li, R. F. [1 ]
Qi, K. [1 ]
机构：
[1] Shanghai Univ Engn Sci, Coll Mat Engn, Shanghai 200336, Peoples R China
来源：
MATERIALS SCIENCE AND TECHNOLOGY | 2006年 / 22卷 / 07期
关键词：
Al2O3; ceramic; brazing; crack; Ti-Cu-Ni filler metal; intermetallic compound;
D O I：
10.1179/174328406X102435
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Joining of metal to ceramic is difficult owing to the formation of cracks at the interface of brazed joint. In the present paper, the crack forming metallurgical mechanisms is studied primarily. The vacuum brazing experiments of ceramic Al2O3 and Kovar, Ni, Fe or Co metals are all conducted. It can be obtained that the cracks could be formed at the Al2O3-Kovar and Al2O3-Fe joint, but not at the Al2O3-Ni and Al2O3-Co joint. In addition, the interfacial morphology and compound composition near cracks are confirmed. It can be concluded that the formation of intermetallic compound FexTiy is the main reason why cracks formed.
引用
收藏
页码：864 / 866
页数：3
相关论文
共 50 条
  • [41] Microstructure evolution and bonding strength of the Al2O3/Al2O3 interface brazed via Ni-Ti intermetallic phases
    Lu, Yao
    Zhu, Meixiong
    Zhang, Qi
    Hu, Tao
    Wang, Juan
    Zheng, Kaihong
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2020, 40 (04) : 1496 - 1504
  • [42] Enhanced bonding of Al2O3/Al2O3 joints brazed by Ni50Ti50 master alloy interlayer
    Zhang, Qi
    Lu, Yao
    Wang, Juan
    Zheng, Kaihong
    Xue, Wenying
    Yang, Hongwang
    VACUUM, 2021, 185
  • [43] Microstructural stability and mechanical properties of Al2O3/Kovar 4 J34 joint vacuum brazed using Ag-5Cu-1Al-1.25Ti (wt%) filler metal
    Wang, J. L.
    Yang, Z. W.
    Wang, Y.
    Wang, D. P.
    Li, H. J.
    JOURNAL OF MANUFACTURING PROCESSES, 2021, 72 : 553 - 564
  • [44] Effect of Cu interlayer with different thickness on microstructure and properties of Al2O3/Kovar joints brazed with Cu–Ti/Cu/BNi-2 composite filler
    Anhang Li
    Tao Wang
    Xiaoguang Chen
    Weibing Guo
    Haitao Xue
    Cuixin Chen
    Journal of Materials Science: Materials in Electronics, 2024, 35
  • [45] RISING CRACK-GROWTH-RESISTANCE BEHAVIOR OF AL2O3 AND AL2O3 + SIC WHISKER CERAMICS
    DUSZA, J
    BARINOV, SM
    SCRIPTA METALLURGICA ET MATERIALIA, 1993, 28 (04): : 417 - 422
  • [46] Interfacial morphology and strength of Al2O3/Nb joint brazed with Cu-Ti-Zr filler metal
    Yu, ZS
    Wu, MF
    Liang, C
    Wang, FJ
    Qi, K
    MATERIALS SCIENCE AND TECHNOLOGY, 2002, 18 (01) : 99 - 102
  • [47] Effect of sulfiding temperatures on the formation of sulfides of Mo/Al2O3 and CoMo/Al2O3
    Kim, Seo Il, 1600, (74):
  • [48] EFFECT OF SULFIDING TEMPERATURES ON THE FORMATION OF SULFIDES OF MO/AL2O3 AND COMO/AL2O3
    SEO, IK
    SEONG, IW
    APPLIED CATALYSIS, 1991, 74 (01): : 109 - 123
  • [49] THERMODYNAMIC ANALYSIS OF ALUMINATE FORMATION AT FE/AL2O3 AND CU/AL2O3 INTERFACES
    TRUMBLE, KP
    ACTA METALLURGICA ET MATERIALIA, 1992, 40 : S105 - S110
  • [50] Formation and microstructure of β/β"-Al2O3 film on a spinel-α-Al2O3 composite substrate
    Wen, ZY
    Lin, ZX
    Jiang, DL
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1998, 17 (04) : 323 - 325
12345