Crack formation mechanisms in Al2O3/Kovar brazed joint

被引：6
|
作者：
Yu, Z. S. [1 ]
Yang, P. [1 ]
Li, R. F. [1 ]
Qi, K. [1 ]
机构：
[1] Shanghai Univ Engn Sci, Coll Mat Engn, Shanghai 200336, Peoples R China
来源：
MATERIALS SCIENCE AND TECHNOLOGY | 2006年 / 22卷 / 07期
关键词：
Al2O3; ceramic; brazing; crack; Ti-Cu-Ni filler metal; intermetallic compound;
D O I：
10.1179/174328406X102435
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Joining of metal to ceramic is difficult owing to the formation of cracks at the interface of brazed joint. In the present paper, the crack forming metallurgical mechanisms is studied primarily. The vacuum brazing experiments of ceramic Al2O3 and Kovar, Ni, Fe or Co metals are all conducted. It can be obtained that the cracks could be formed at the Al2O3-Kovar and Al2O3-Fe joint, but not at the Al2O3-Ni and Al2O3-Co joint. In addition, the interfacial morphology and compound composition near cracks are confirmed. It can be concluded that the formation of intermetallic compound FexTiy is the main reason why cracks formed.
引用
收藏
页码：864 / 866
页数：3
相关论文
共 50 条
  • [31] Microstructure evolution and strengthening mechanism of Al2O3/Kovar joints brazed with TiB enhanced Ag-Cu-Ti based composite fillers
    Ma, Guo-Fu
    Li, Xiao-Qiang
    Jiang, Qi
    Zhu, De-Zhi
    Yang, Chao
    VACUUM, 2025, 238
  • [32] FORMATION OF ALPHA AL2O3 IN ALUM-DERIVED GAMMA AL2O3
    DYNYS, FW
    HALLORAN, JW
    AMERICAN CERAMIC SOCIETY BULLETIN, 1980, 59 (03): : 361 - 361
  • [33] Residual stress distribution of the soldered structure with Kovar alloy and Al2O3 ceramics
    Gao, Qile
    Wang, Jing
    Zhang, Yiliang
    Zhou, Junming
    Peng, Jiagen
    Hu, Shouliang
    Zeng, Yanjun
    PROCESSING AND APPLICATION OF CERAMICS, 2017, 11 (01) : 75 - 81
  • [34] Al2O3/Kovar钎焊接头裂纹冶金因素分析
    杨沛
    于治水
    祁凯
    余春
    李瑞峰
    华东船舶工业学院学报(自然科学版), 2005, (01) : 86 - 89
  • [35] Effects of Al2O3 Particulates on the Thickness of Reaction Layer of Al2O3 Joints Brazed with Al2O3-Particulate-Contained Composite Filler Materials
    Jianguo YANG
    Journal of Materials Science & Technology, 2003, (05) : 509 - 510
  • [36] Relevance and formation mechanisms of negative ions upon ablation of Al2O3
    Pelaez, R. J.
    Afonso, C. N.
    Chen, J.
    Esposito, M.
    Lippert, Th
    Stender, D.
    Wokaun, A.
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2012, 45 (28)
  • [37] Study on preparation and formation mechanisms of Al2O3 nanoparticles by reverse microemulsion
    Huang Ke-Long
    Yin Liang-Guo
    Liu Su-Qin
    ACTA CHIMICA SINICA, 2007, 65 (04) : 310 - 314
  • [38] Effects of Al2O3 particulates on the thickness of reaction layer of Al2O3 joints brazed with Al2O3-particulate-contained composite filler materials
    Yang, JG
    Wu, JW
    Fang, HY
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2003, 19 (05) : 509 - 510
  • [39] Deformation and fracture mechanisms of Al2O3/Nb/Al2O3 composites under compression
    Zhang, ZF
    Brunner, D
    Scheu, C
    Rühle, M
    ZEITSCHRIFT FUR METALLKUNDE, 2005, 96 (01): : 62 - 70
  • [40] Role of Ti diffusion on the formation of phases in the Al2O3-Al2O3 brazed interface
    Kar, Abhijit
    Mandal, Sudipta
    Ghosh, Rabindra N.
    Ghosh, Tamal K.
    Ray, Ajoy Kumar
    JOURNAL OF MATERIALS SCIENCE, 2007, 42 (14) : 5556 - 5561
12345