Stress Relief Cracking in Advanced Steel Material- Overview

被引：0

作者：

Ghiya, S. P. ^{[1
]}

Bhatt, D. V. ^{[2
]}

Rao, R. V. ^{[2
]}

机构：

[1] SVNIT, Surat, India

[2] SVNIT, Dept Mech Engn, Surat, India

来源：

WORLD CONGRESS ON ENGINEERING 2009, VOLS I AND II | 2009年

关键词：

Cr; Mo; V alloy steel; Stress Relief Crack; Molybdenum carbide; Vanadium carbide;

D O I：

暂无

中图分类号：

TP301 [理论、方法];

学科分类号：

081202 ;

摘要：

This paper summarizes the. quality problems of the weldability of advanced vanadium modified Cr, Mo alloy steel material, during fabrication of reactor, pressure vessel being used for Refinery, Petrochemical, Chemical plants. Authors have focused on stress relief cracking occurred in weld metal and HAZ after stress relieving heat treatment of the weld. From the literature review, it appears that till date significant amount of efforts are made to understand the stress relief cracking, occurring in alloy steel. However considerable work is still being done on this quality issue to understand root cause of stress relief cracking and remedy to prevent it.

引用

页码：1737 / +

页数：2

共 50 条

[41] An overview of heat stress relief with global warming in perspective
Berman, A.
INTERNATIONAL JOURNAL OF BIOMETEOROLOGY, 2019, 63 (04) : 493 - 498
[42] STRESS-CORROSION CRACKING - A MATERIAL PROBLEM
KOSTERS, K
HASELMAIR, H
PONSCHAB, H
WALLNER, F
STAHL UND EISEN, 1982, 102 (15-1): : 779 - 785
[43] Influence of ultrasonic stress relief on stainless steel 316 specimens: A comparison with thermal stress relief
Shalvandi, M.
Hojjat, Y.
Abdullah, A.
Asadi, H.
MATERIALS & DESIGN, 2013, 46 : 713 - 723
[44] Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: part I—effect of heat control on welding stresses and stress relief cracking
A. Kromm
T. Lausch
D. Schroepfer
M. Rhode
T. Kannengiesser
Welding in the World, 2020, 64 : 807 - 817
[45] AN OVERVIEW - PREVENTION AND CONTROL OF STRESS-CORROSION CRACKING
PARKINS, RN
MATERIALS PERFORMANCE, 1985, 24 (08) : 9 - 20
[46] STRESS-CORROSION CRACKING OF STEEL WELDMENTS
FUJII, CT
METZBOWER, EA
METALS ENGINEERING QUARTERLY, 1976, 16 (04): : 15 - 20
[47] Stress corrosion cracking of carbon steel weldments
Lam, Poh-Sang
Sindelar, Robert L.
Cheng, Changmin
Stefek, Tina M.
Chao, Yuh J.
Elder, James B., III
PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE 2005, VOL 6, 2005, 6 : 155 - 163
[48] STRESS CORROSION CRACKING OF AUSTENITIC STAINLESS STEEL
MAREK, M
HOCHMAN, RF
CORROSION, 1970, 26 (01) : 5 - &
[49] STRESS-CORROSION CRACKING OF STEEL WELDMENTS
FUJII, CT
REPORT OF NRL PROGRESS, 1975, (NOV): : 25 - 26
[50] On the resistance of duplex steel to stress corrosion cracking
Cihal, V.
Werkstoffe und Korrosion, 1992, 43 (11): : 532 - 537

← 1 2 3 4 5 →