Stress Relief Cracking in Advanced Steel Material- Overview

被引：0
|
作者：
Ghiya, S. P. [1 ]
Bhatt, D. V. [2 ]
Rao, R. V. [2 ]
机构：
[1] SVNIT, Surat, India
[2] SVNIT, Dept Mech Engn, Surat, India
来源：
WORLD CONGRESS ON ENGINEERING 2009, VOLS I AND II | 2009年
关键词：
Cr; Mo; V alloy steel; Stress Relief Crack; Molybdenum carbide; Vanadium carbide;
D O I：
暂无
中图分类号：
TP301 [理论、方法];
学科分类号：
081202 ;
摘要：
This paper summarizes the. quality problems of the weldability of advanced vanadium modified Cr, Mo alloy steel material, during fabrication of reactor, pressure vessel being used for Refinery, Petrochemical, Chemical plants. Authors have focused on stress relief cracking occurred in weld metal and HAZ after stress relieving heat treatment of the weld. From the literature review, it appears that till date significant amount of efforts are made to understand the stress relief cracking, occurring in alloy steel. However considerable work is still being done on this quality issue to understand root cause of stress relief cracking and remedy to prevent it.
引用
收藏
页码：1737 / +
页数：2
相关论文
共 50 条
12345