Polyhydroxybutyrate/Valerate/Polycaprolactone Small-Diameter Vascular Graft: Experimental Study of Integration into Organism

We prepared polyhydroxybutyrate/valerate (PHBV)/polylcaprolactone (PCL) small-diameter vascular grafts using electrospinning. Surface structure was assessed by scanning electron microscopy whilst physicomechanical properties were investigated by longitudinal uniaxial tension testing. Patency of grafts implanted into the rat abdominal aorta was evaluated using a Doppler ultrasonography at 2 week, 1 month and 12 month postimplantation. In addition, we assessed local histological features, along with IL-1 beta, IL-2, IL-4, IL-10, TNF alpha, TGF-beta 1, and VEGF serum levels. We revealed that only 2 (25%) grafts were not thrombosed at 2 week and 1 month postimplantation. However, at 12 month postimplantation a satisfactory histological pattern was observed in 50% of all cases, and we detected a monolayer of endothelial cells on the inner graft surface in half the cases. Regarding other grafts, we revealed minor connective tissue hyperplasia in 41.7% of the grafts and an inflammatory infiltrate in the part of the arterial wall in 8.3% of the grafts. We found that the IL-1 beta serum level was 3.5-fold higher in the group of experimental rats at 12 month postimplantation (p < 0.01). In addition, the IL-2 and IL-4 serum levels at 12 month postimplantation were 2-and 2.8-fold higher as compared to short-term implantation (2 weeks and 1 month) and control rats (p < 0.05) whilst the IL-10 serum level at 1 and 12 month postimplantation was more than 100-fold higher in comparison with 2 week postimplantation and control rats (p < 0.001). Serum VEGF was detected only at 12 month postimplantation. All in all, we created a biocompatible PHBV/PCL small-diameter vascular graft with a high surface area to volume ratio. A long-term patency of biodegradable vascular grafts after implantation into the rat abdominal aorta and the absence of a considerable immune response confirmed a high biocompatibility of such construct and the possibility of its use as a vascular graft.